Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
SMA XIRAN® SE700 POLYSCOPE HOLLAND
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | POLYSCOPE HOLLAND/XIRAN® SE700 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 9.0 kJ/m² |
| Impact strength of simply supported beam without notch | -40°C | ISO 179/1eU | 30 kJ/m² |
| 23°C | ISO 179/1eU | 30 kJ/m² | |
| Charpy Notched Impact Strength | -40°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of cantilever beam gap | -40°C | ISO 180/A | 5.0 kJ/m² |
| 23°C | ISO 180/A | 9.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | POLYSCOPE HOLLAND/XIRAN® SE700 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2100 MPa | |
| tensile strength | 断裂 | ISO 527-2 | 35.0 MPa |
| Tensile strain | 断裂 | ISO 527-2 | 3.0 % |
| tensile strength | 屈服 | ISO 527-2 | 36.0 MPa |
| Flexural modulus | ISO 178 | 8500 MPa | |
| bending strength | ISO 178 | 150 MPa |
| flammability | Test Condition | Test Method | POLYSCOPE HOLLAND/XIRAN® SE700 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | POLYSCOPE HOLLAND/XIRAN® SE700 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.20 % |
| spiral flow length | 内部方法 | 36.0 cm | |
| melt mass-flow rate | 240°C/10.0kg | ISO 1133 | 22 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ASTM D570 | 0.20 % |
| Shrinkage rate | TD | 内部方法 | 0.50 % |
| density | ISO 1183 | 1.05 g/cm³ |
| Thermal performance | Test Condition | Test Method | POLYSCOPE HOLLAND/XIRAN® SE700 |
|---|---|---|---|
| vicat | ISO 306/B | 115 °C | |
| Linear coefficient of thermal expansion | TD：-30to80°C | ASTM D696 | 4.7E-05 cm/cm/°C |
| MD：-30到80°C | ASTM D696 | 2.9E-05 cm/cm/°C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 92.0 °C |