PPA AMODEL® A-1933 HSL BK
258
- Properties:Filler: Glass fiber reinf33% filler by weight
- Usages:Valves/valve componentsParts under the hood of a carApplication in the automotive fieldShell
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.20 % | |
| ASTM D955 | 1.0 % | ||
| ISO 294-4 | 1.0 % | ||
| ISO 294-4 | 0.20 % | ||
| Water absorption rate | ASTM D570 | 0.19 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 11500 Mpa | |
| tensile strength | ISO 527-2 | 195 Mpa | |
| bending strength | ISO 178 | 280 Mpa | |
| Tensile strain | ISO 527-2 | 1.8 % | |
| Flexural modulus | ISO 178 | 10300 Mpa |
| aging | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Flexural Retention Modulus-1000hr, in Glycol | ISO 178 | 76 % | |
| Retention ofFlexuralStrength-1000hr,in Glycol | ISO 178 | 71 % | |
| Tensile Retention Modulus-1000hr, in Glycol | ISO 527-2 | 75 % | |
| Retention of Tensile Strength-1000hr, in Glycol | ISO 527-2 | 69 % |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/A | 295 °C | |
| melting temperature | ISO 11357-3 | 323 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.