PPA A-1933 HSL BK SOLVAY USA
AMODEL®
Valves/valve components、Parts under the hood of a、Application in the automo、Shell
Filler: Glass fiber reinf、33% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | SOLVAY USA/A-1933 HSL BK |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 11500 Mpa | |
| bending strength | ISO 178 | 280 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.8 % |
| Flexural modulus | ISO 178 | 10300 Mpa | |
| tensile strength | 屈服 | ISO 527-2 | 195 Mpa |
| physical property | Test Condition | Test Method | SOLVAY USA/A-1933 HSL BK |
|---|---|---|---|
| Shrinkage rate | TD | ISO 294-4 | 1.0 % |
| MD | ISO 294-4 | 0.20 % | |
| Water absorption rate | 24hr | ASTM D570 | 0.19 % |
| Shrinkage rate | TD2 | ASTM D955 | 1.0 % |
| MD2 | ASTM D955 | 0.20 % |
| aging | Test Condition | Test Method | SOLVAY USA/A-1933 HSL BK |
|---|---|---|---|
| Tensile Retention Modulus-1000hr, in Glycol | 130°C | ISO 527-2 | 75 % |
| Retention ofFlexuralStrength-1000hr,in Glycol | 130°C | ISO 178 | 71 % |
| Flexural Retention Modulus-1000hr, in Glycol | 130°C | ISO 178 | 76 % |
| Retention of Tensile Strength-1000hr, in Glycol | 130°C | ISO 527-2 | 69 % |
| Thermal performance | Test Condition | Test Method | SOLVAY USA/A-1933 HSL BK |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 323 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 295 °C |