PC/PBT XENOY™ 5720U-YW5E108 SABIC INNOVATIVE US
156
- Properties:Chemical resistanceLow temperature impact re
- Usages:Plastic bagLighting applicationsHousehold daily necessiti
Compare
View PricesTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 特定体积 | ASTM D792 | 0.850 cm³/g | |
| 熔体质量流动速率 | 250°C/2.16 kg | ASTM D1238 | 3.8 g/10 min |
| 250°C/5.0 kg | ASTM D1238, ISO 1133 | 11 g/10 min | |
| 265°C/2.16 kg | ASTM D1238 | 6.0 g/10 min | |
| 266°C/5.0 kg | ASTM D1238 | 20 g/10 min | |
| 250°C/2.16 kg | ISO 1133 | 3.0 g/10 min | |
| 熔融体积流量（MVR） | 250°C/2.16 kg | ISO 1133 | 3.00 cm3/10min |
| 250°C/5.0 kg | ISO 1133 | 10.0 cm3/10min | |
| 265°C/2.16 kg | ISO 1133 | 6.00 cm3/10min | |
| 265°C/5.0 kg | ISO 1133 | 18.0 cm3/10min | |
| 收缩率 - 流动 | 3.20 mm | 内部方法 | 1.0 到 1.2 % |
| 吸水率 | 饱和, 23°C | ISO 62 | 0.28 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.080 % |
| 热性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 载荷下热变形温度 | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 108 °C |
| 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 117 °C | |
| 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 12 | ISO 75-2/Bf | 109 °C | |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 83.0 °C | |
| 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 95.0 °C | |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 12 | ISO 75-2/Af | 87.0 °C | |
| 维卡软化温度 | -- | ASTM D152513, ISO 306/B5013 | 119 °C |
| -- | ISO 306/B120 | 122 °C | |
| 线性热膨胀系数 | 流动 : -40 到 95°C | ASTM E831 | 9.8E-5 cm/cm/°C |
| 流动 : -30 到 80°C | ISO 11359-2 | 9.8E-5 cm/cm/°C | |
| 横向 : -40 到 95°C | ASTM E831 | 1.0E-4 cm/cm/°C | |
| 横向 : -30 到 80°C | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 拉伸模量 | -- 2 | ASTM D638 | 1830 Mpa |
| -- 3 | 内部方法 | 1830 Mpa | |
| -- 4 | ASTM D638 | 1810 Mpa | |
| -- | ISO 527-2/1 | 1790 Mpa | |
| 抗张强度 | 屈服 5 | ASTM D638 | 47.0 Mpa |
| 屈服 6 | 内部方法 | 45.0 Mpa | |
| 屈服 7 | ASTM D638 | 44.0 Mpa | |
| 屈服 | ISO 527-2/5 | 44.0 Mpa | |
| 屈服 | ISO 527-2/50 | 47.0 Mpa | |
| 断裂 7 | ASTM D638 | 50.0 Mpa | |
| 断裂 6 | 内部方法 | 47.0 Mpa | |
| 断裂 5 | ASTM D638 | 48.0 Mpa | |
| 断裂 | ISO 527-2/5, ISO 527-2/50 | 43.0 Mpa | |
| 伸长率 | 屈服 7 | ASTM D638 | 4.6 % |
| 屈服 6 | 内部方法 | 4.6 % | |
| 屈服 5 | ASTM D638 | 4.0 % | |
| 屈服 | ISO 527-2/5 | 4.1 % | |
| 屈服 | ISO 527-2/50 | 4.6 % | |
| 断裂 7 | ASTM D638 | 120 % | |
| 断裂 6 | 内部方法 | 110 % | |
| 断裂 5 | ASTM D638 | 120 % | |
| 断裂 | ISO 527-2/5 | 110 % | |
| 断裂 | ISO 527-2/50 | 120 % | |
| 弯曲模量 | 50.0 mm 跨距 8 | ASTM D790 | 1660 Mpa |
| -- 9 | ISO 178 | 1860 Mpa | |
| 弯曲应力 | -- 9, 10 | ISO 178 | 71.0 Mpa |
| 屈服, 50.0 mm 跨距 8 | ASTM D790 | 70.0 Mpa | |
| 断裂, 50.0 mm 跨距 8 | ASTM D790 | 69.0 Mpa |
| 注射 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 干燥温度 | 110 °C | ||
| 干燥时间 | 4.0 到 6.0 hr | ||
| 建议的最大水分含量 | 0.020 % | ||
| 建议注射量 | 50 到 80 % | ||
| 料筒后部温度 | 245 到 265 °C | ||
| 料筒中部温度 | 250 到 270 °C | ||
| 料筒前部温度 | 255 到 275 °C | ||
| 射嘴温度 | 255 到 270 °C | ||
| 加工（熔体）温度 | 260 到 275 °C | ||
| 模具温度 | 65 到 90 °C | ||
| 背压 | 0.300 到 0.700 Mpa | ||
| 螺杆转速 | 50 到 80 rpm | ||
| 排气孔深度 | 0.013 到 0.020 mm |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 简支梁缺口冲击强度 11 | -30°C | ISO 179/1eA | 47 kJ/m² |
| 23°C | ISO 179/1eA | 55 kJ/m² | |
| 装有测量仪表的落镖冲击 | -40°C, Energy at Peak | ASTM D3763 | 49.0 J |
| -40°C, Total Energy | ASTM D3763 | 59.0 J | |
| -30°C, Energy at Peak | ASTM D3763 | 49.0 J | |
| -30°C, Total Energy | ASTM D3763 | 61.0 J | |
| -20°C, Energy at Peak | ASTM D3763 | 41.0 J | |
| -20°C, Total Energy | ASTM D3763 | 53.0 J | |
| 23°C, Energy at Peak | ASTM D3763 | 44.0 J | |
| 23°C, Total Energy | ASTM D3763 | 54.0 J |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.