Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/PBT 5720U-YW5E108 SABIC INNOVATIVE US
XENOY™
Plastic bag、Lighting applications、Household daily necessiti
Chemical resistance、Low temperature impact re
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/5720U-YW5E108 |
|---|---|---|---|
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 95.0 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 12 | ISO 75-2/Af | 87.0 °C | |
| 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 117 °C | |
| Vicat Softening Temperature | -- | ISO 306/B120 | 122 °C |
| Linear thermal expansion coefficient | 横向 : -40 到 95°C | ASTM E831 | 1.0E-4 cm/cm/°C |
| Deflection Temperature Under Load? | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 83.0 °C |
| Linear thermal expansion coefficient | 横向 : -30 到 80°C | ISO 11359-2 | 1.0E-4 cm/cm/°C |
| Vicat Softening Temperature | -- | ASTM D152513, ISO 306/B5013 | 119 °C |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 108 °C |
| Linear thermal expansion coefficient | 流动 : -40 到 95°C | ASTM E831 | 9.8E-5 cm/cm/°C |
| Deflection Temperature Under Load? | 0.45 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 12 | ISO 75-2/Bf | 109 °C |
| Linear thermal expansion coefficient | 流动 : -30 到 80°C | ISO 11359-2 | 9.8E-5 cm/cm/°C |
| Injection | Test Condition | Test Method | SABIC INNOVATIVE US/5720U-YW5E108 |
|---|---|---|---|
| Middle Temperature | 250 到 270 °C | ||
| Drying Time | 4.0 到 6.0 hr | ||
| Suggested Shot Size | 50 到 80 % | ||
| Drying Temperature | 110 °C | ||
| Mold Temperature | 65 到 90 °C | ||
| Vent Depth | 0.013 到 0.020 mm | ||
| Suggested Max Moisture | 0.020 % | ||
| Processing (Melt) Temp | 260 到 275 °C | ||
| Rear Temperature | 245 到 265 °C | ||
| Nozzle Temperature | 255 到 270 °C | ||
| Front Temperature | 255 到 275 °C | ||
| Back Pressure | 0.300 到 0.700 Mpa | ||
| Screw Speed | 50 到 80 rpm |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/5720U-YW5E108 |
|---|---|---|---|
| Melt Mass-Flow Rate | 265°C/2.16 kg | ASTM D1238 | 6.0 g/10 min |
| Moisture Absorption | 平衡, 23°C, 50% RH | ISO 62 | 0.080 % |
| Melt Mass-Flow Rate | 266°C/5.0 kg | ASTM D1238 | 20 g/10 min |
| Melt Volume flow Rate | 265°C/5.0 kg | ISO 1133 | 18.0 cm3/10min |
| Melt Mass-Flow Rate | 250°C/2.16 kg | ASTM D1238 | 3.8 g/10 min |
| Melt Volume flow Rate | 250°C/5.0 kg | ISO 1133 | 10.0 cm3/10min |
| Specific Volume | ASTM D792 | 0.850 cm³/g | |
| Melt Volume flow Rate | 250°C/2.16 kg | ISO 1133 | 3.00 cm3/10min |
| Melt Mass-Flow Rate | 250°C/2.16 kg | ISO 1133 | 3.0 g/10 min |
| Melt Volume flow Rate | 265°C/2.16 kg | ISO 1133 | 6.00 cm3/10min |
| Melt Mass-Flow Rate | 250°C/5.0 kg | ASTM D1238, ISO 1133 | 11 g/10 min |
| Modeling Shrinkage - Flow | 3.20 mm | 内部方法 | 1.0 到 1.2 % |
| Moisture Absorption | 饱和, 23°C | ISO 62 | 0.28 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/5720U-YW5E108 |
|---|---|---|---|
| Tensile Elongation | 屈服 7 | ASTM D638 | 4.6 % |
| 断裂 | ISO 527-2/5 | 110 % | |
| Flexural Stress | 断裂, 50.0 mm 跨距 8 | ASTM D790 | 69.0 Mpa |
| Tensile Elongation | 屈服 6 | 内部方法 | 4.6 % |
| 屈服 | ISO 527-2/50 | 4.6 % | |
| Flexural Stress | 屈服, 50.0 mm 跨距 8 | ASTM D790 | 70.0 Mpa |
| Tensile Modulus | -- 2 | ASTM D638 | 1830 Mpa |
| Tensile Strength | 屈服 6 | 内部方法 | 45.0 Mpa |
| Tensile Modulus | -- 4 | ASTM D638 | 1810 Mpa |
| Tensile Strength | 断裂 5 | ASTM D638 | 48.0 Mpa |
| Tensile Modulus | -- 3 | 内部方法 | 1830 Mpa |
| Tensile Strength | 屈服 | ISO 527-2/5 | 44.0 Mpa |
| 断裂 7 | ASTM D638 | 50.0 Mpa | |
| Tensile Elongation | 断裂 | ISO 527-2/50 | 120 % |
| Flexural Modulus | -- 9 | ISO 178 | 1860 Mpa |
| Flexural Stress | -- 9, 10 | ISO 178 | 71.0 Mpa |
| Tensile Modulus | -- | ISO 527-2/1 | 1790 Mpa |
| Tensile Strength | 断裂 6 | 内部方法 | 47.0 Mpa |
| Tensile Elongation | 断裂 5 | ASTM D638 | 120 % |
| 断裂 6 | 内部方法 | 110 % | |
| Flexural Modulus | 50.0 mm 跨距 8 | ASTM D790 | 1660 Mpa |
| Tensile Strength | 屈服 5 | ASTM D638 | 47.0 Mpa |
| 屈服 7 | ASTM D638 | 44.0 Mpa | |
| 屈服 | ISO 527-2/50 | 47.0 Mpa | |
| Tensile Elongation | 屈服 | ISO 527-2/5 | 4.1 % |
| 断裂 7 | ASTM D638 | 120 % | |
| 屈服 5 | ASTM D638 | 4.0 % | |
| Tensile Strength | 断裂 | ISO 527-2/5, ISO 527-2/50 | 43.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/5720U-YW5E108 |
|---|---|---|---|
| Instrumented Dart Impact | -20°C, Total Energy | ASTM D3763 | 53.0 J |
| -20°C, Energy at Peak | ASTM D3763 | 41.0 J | |
| 23°C, Total Energy | ASTM D3763 | 54.0 J | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 47 kJ/m² |
| 23°C | ISO 179/1eA | 55 kJ/m² | |
| Instrumented Dart Impact | 23°C, Energy at Peak | ASTM D3763 | 44.0 J |
| -30°C, Energy at Peak | ASTM D3763 | 49.0 J | |
| -30°C, Total Energy | ASTM D3763 | 61.0 J | |
| -40°C, Energy at Peak | ASTM D3763 | 49.0 J | |
| -40°C, Total Energy | ASTM D3763 | 59.0 J |