PC LUBEXAN 1015 GREY TQ
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183/A | 1.17to1.21 g/cm³ | |
| melt mass-flow rate | ISO 1133 | 10to15 g/10min | |
| Water absorption rate | ISO 62 | 0.15 % | |
| ISO 62 | 0.36 % |
| flammability | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Burning wire flammability index | IEC 60695-2-12 | 850 °C |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256 | 无断裂 | |
| ASTM D256 | 45to55 kJ/m² | ||
| Charpy Notched Impact Strength | ISO 179/1eA | 25to30 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 无断裂 | |
| Impact strength of cantilever beam gap | ASTM D256A | 450to550 J/m | |
| ISO 180/A | 25to30 kJ/m² | ||
| Suspended wall beam without notch impact strength | ISO 180 | 无断裂 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| bending strength | ISO 178 | 50.0to60.0 MPa | |
| Tensile strain | Yield | ISO 527-2/1A/50 | 4.0to7.0 % |
| Break | ISO 527-2/1A/50 | 15to20 % | |
| Flexural modulus | ISO 178 | 1800to2200 MPa | |
| Tensile modulus | ISO 527-2/1A/1 | 2000to2500 MPa | |
| tensile strength | Yield | ISO 527-2/1A/50 | 45.0to50.0 MPa |
| Break | ISO 527-2/1A/50 | 40.0to45.0 MPa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 130to140 °C | |
| ISO 75-2/B | 135to145 °C | ||
| ASTM D648 | 120to130 °C | ||
| Glass Transition Temperature | 内部方法 | 140to150 °C | |
| vicat | ISO 306/A120 | 140to150 °C | |
| ISO 306/B120 | 135to145 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.