PC LUBEXAN 1015 GREY TQ LUBEN PLAST srl
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LUBEN PLAST srl/LUBEXAN 1015 GREY TQ |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C4 | ASTM D256 | 45to55 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 25to30 kJ/m² |
| Impact strength of cantilever beam gap | 23°C3 | ASTM D256 | 无断裂 |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 无断裂 |
| Impact strength of cantilever beam gap | 23°C,3.20mm | ASTM D256A | 450to550 J/m |
| Suspended wall beam without notch impact strength | 23°C | ISO 180 | 无断裂 |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 25to30 kJ/m² |
| Mechanical properties | Test Condition | Test Method | LUBEN PLAST srl/LUBEXAN 1015 GREY TQ |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 4.0to7.0 % |
| 断裂 | ISO 527-2/1A/50 | 15to20 % | |
| tensile strength | 断裂 | ISO 527-2/1A/50 | 40.0to45.0 MPa |
| Tensile modulus | ISO 527-2/1A/1 | 2000to2500 MPa | |
| Flexural modulus | ISO 178 | 1800to2200 MPa | |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 45.0to50.0 MPa |
| bending strength | ISO 178 | 50.0to60.0 MPa |
| flammability | Test Condition | Test Method | LUBEN PLAST srl/LUBEXAN 1015 GREY TQ |
|---|---|---|---|
| Burning wire flammability index | 2.0mm | IEC 60695-2-12 | 850 °C |
| physical property | Test Condition | Test Method | LUBEN PLAST srl/LUBEXAN 1015 GREY TQ |
|---|---|---|---|
| Water absorption rate | 23°C,24hr,3.20mm | ISO 62 | 0.15 % |
| density | ISO 1183/A | 1.17to1.21 g/cm³ | |
| Water absorption rate | 饱和,23°C,3.20mm | ISO 62 | 0.36 % |
| melt mass-flow rate | 300°C/1.2kg | ISO 1133 | 10to15 g/10min |
| Thermal performance | Test Condition | Test Method | LUBEN PLAST srl/LUBEXAN 1015 GREY TQ |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 135to145 °C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 135to145 °C |
| vicat | -- | ISO 306/A120 | 140to150 °C |
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 130to140 °C |
| Glass Transition Temperature | 内部方法 | 140to150 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 120to130 °C |