POM TENAC™-C Z3510
43
- Properties:High impact resistanceMedium viscosity
- Usages:Electrical applicationsHousehold daily necessitiesShellApplication in the automotive fieldEngine partsEngineering accessories
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO 1133 | 2.8 g/10min | |
| Shrinkage rate | 内部方法 | 1.6-2.0 % | |
| Water absorption rate | ASTM D570 | 0.20 % |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Rockwell hardness | ASTM D785 | 78 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2500 Mpa | |
| tensile strength | ISO 527-2 | 62.0 Mpa | |
| ASTM D638 | 62.0 Mpa | ||
| elongation | ASTMD638 | 40 % | |
| Flexural modulus | ASTM D790 | 2450 Mpa | |
| ISO 178 | 2400 Mpa | ||
| bending strength | ASTM D790 | 88.0 Mpa | |
| Taber abraser | ASTM D1044 | 14.0 mg |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1.0E+15-1.0E+16 ohms·cm | |
| dielectric strength | ASTM D149 | 19 KV/mm | |
| dielectric constant | ASTM D150 | 3.90 | |
| Dissipation Factor | ASTM D150 | 8E-03 | |
| arc resistance | ASTM D495 | 250 sec | |
| Surface Resistivity | ASTM D257 | 1.0E+16-1.0E+17 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 158 °C | |
| ISO 75-2/B | 156 °C | ||
| ASTM D648 | 110 °C | ||
| ISO 75-2/A | 95.0 °C | ||
| Linear coefficient of thermal expansion | ASTMD696 | 1E-04 cm/cm/°C | |
| specific heat | 1470 J/kg/°C | ||
| thermal conductivity | 0.23 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.