Technical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 熔体质量流动速率 | 337°C/6.6 kg | ASTM D1238 | 11 g/10 min |
| 热性能 | Test Condition | Test Method | Test Result |
|---|
| 载荷下热变形温度 | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 207 °C |
| RTI Elec | | UL 746 | 170 °C |
| RTI Imp | | UL 746 | 170 °C |
| RTI | | UL 746 | 170 °C |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|
| UL阻燃等级 | 0.41 mm | UL 94 | V-0 |
| UL阻燃等级 | 1.9 mm | UL 94 | 5VA |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 拉伸模量 2 | | ASTM D638 | 4610 Mpa |
| 抗张强度 3 | 屈服 | ASTM D638 | 114 Mpa |
| 抗张强度 3 | 断裂 | ASTM D638 | 115 Mpa |
| 伸长率 | 断裂 | ASTM D638 | 6.0 % |
| 弯曲模量 | 100 mm 跨距 | ASTM D790 | 5240 Mpa |
| 弯曲强度 | 断裂, 100 mm 跨距 | ASTM D790 | 199 Mpa |
| 电气性能 | Test Condition | Test Method | Test Result |
|---|
| 耐电弧性 5 | | ASTM D495 | PLC 6 |
| 相比耐漏电起痕指数(CTI) | | UL 746 | PLC 4 |
| 高电弧燃烧指数(HAI) | | UL 746 | PLC 4 |
| 高电压电弧起痕速率(HVTR) | | UL 746 | PLC 2 |
| 热丝引燃(HWI) | | UL 746 | PLC 1 |
| 注射 | Test Condition | Test Method | Test Result |
|---|
| 干燥温度 | | | 150 °C |
| 干燥时间 | | | 4.0 到 6.0 hr |
| 建议的最大水分含量 | | | 0.020 % |
| 建议注射量 | | | 40 到 60 % |
| 料筒后部温度 | | | 330 到 400 °C |
| 料筒中部温度 | | | 340 到 400 °C |
| 料筒前部温度 | | | 345 到 400 °C |
| 射嘴温度 | | | 345 到 400 °C |
| 加工（熔体）温度 | | | 350 到 400 °C |
| 模具温度 | | | 135 到 165 °C |
| 背压 | | | 0.300 到 0.700 Mpa |
| 螺杆转速 | | | 40 到 70 rpm |
| 排气孔深度 | | | 0.025 到 0.076 mm |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|
| 反向缺口冲击 | 3.20 mm | ASTM D256 | 400 J/m |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.