PA66 Vydyne® 66H NT0694
0
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ISO 1183 | 1.14 g/cm³ | |
| Shrinkage rate | ISO 294-4 | 2.1 % | |
| ISO 294-4 | 2.2 % | ||
| Water absorption rate | ISO 62 | 8.5 % | |
| ISO 62 | 2.5 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | 7.0 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | NoBreak | |
| ISO 179/1eU | NoBreak | ||
| Impact strength of cantilever beam gap | ISO 180 | 6.0 kJ/m² | |
| ISO 180 | 7.0 kJ/m² | ||
| Charpy Notched Impact Strength | ISO 179/1eA | 6.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2850 MPa | |
| tensile strength | ISO 527-2 | 85.0 MPa | |
| ISO 527-2 | 55.0 MPa | ||
| Tensile strain | ISO 527-2 | 5.0 % | |
| Nominal tensile fracture strain | ISO 527-2 | 40 % | |
| Flexural modulus | ISO 178 | 3000 MPa | |
| bending strength | ISO 178 | 80.0 MPa | |
| Poisson's ratio | ISO 527-2 | 0.40 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | IEC 60093 | 1E+14 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ISO 75-2/B | 200 °C | |
| ISO 75-2/A | 65.0 °C | ||
| melting temperature | ISO 11357-3 | 260 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 1E-04 cm/cm/°C | |
| ISO 11359-2 | 1E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.