PA66 Vydyne® 66H NT0694 Ascend Performance Materials Operations LLC
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Ascend Performance Materials Operations LLC/Vydyne® 66H NT0694 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 7.0 kJ/m² |
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
| 23°C | ISO 179/1eU | NoBreak | |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 6.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 7.0 kJ/m² |
| -30°C | ISO 180 | 6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Ascend Performance Materials Operations LLC/Vydyne® 66H NT0694 |
|---|---|---|---|
| Volume resistivity | 0.750mm | IEC 60093 | 1E+14 ohms·cm |
| Mechanical properties | Test Condition | Test Method | Ascend Performance Materials Operations LLC/Vydyne® 66H NT0694 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 3000 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 2850 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 85.0 MPa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 5.0 % |
| tensile strength | 断裂,23°C | ISO 527-2 | 55.0 MPa |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 40 % |
| Poisson's ratio | ISO 527-2 | 0.40 | |
| bending strength | 23°C | ISO 178 | 80.0 MPa |
| physical property | Test Condition | Test Method | Ascend Performance Materials Operations LLC/Vydyne® 66H NT0694 |
|---|---|---|---|
| Shrinkage rate | MD:23°C,2.00mm | ISO 294-4 | 2.2 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 2.5 % |
| 饱和,23°C | ISO 62 | 8.5 % | |
| density | ISO 1183 | 1.14 g/cm³ | |
| Shrinkage rate | TD:23°C,2.00mm | ISO 294-4 | 2.1 % |
| Thermal performance | Test Condition | Test Method | Ascend Performance Materials Operations LLC/Vydyne® 66H NT0694 |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 260 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 200 °C |
| Linear coefficient of thermal expansion | TD：23to55°C,2.00mm | ISO 11359-2 | 1E-04 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 65.0 °C |
| Linear coefficient of thermal expansion | MD：23to55°C,2.00mm | ISO 11359-2 | 1E-04 cm/cm/°C |