Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ASTMD570 | 0.30 % |
| Water absorption rate | Saturation | ASTMD570 | 6.0 % |
| density | | ASTMD792 | 1.15 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | M-Scale | ASTMD785 | 80 |
| Rockwell hardness | R-Scale | ASTMD785 | 117 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| PressureVelocity | | 内部方法 | 0.193 MPa·m/s |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTMD638 | 3450 MPa |
| tensile strength | Ultimate | ASTMD638 | 68.9 MPa |
| elongation | Break | ASTMD638 | 30 % |
| Flexural modulus | | ASTMD790 | 3450 MPa |
| bending strength | Yield | ASTMD790 | 103 MPa |
| Compression Modulus | | ASTMD695 | 2930 MPa |
| compressive strength | | ASTMD695 | 89.6 MPa |
| Steel - Static | 内部方法 | 0.18 |
| Wear factor | | ASTMD3702 | 130 10^-8mm³/N·m |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTMD256A | 48 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | 内部方法 | >1.0E+13 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ASTMD648 | 93.3 °C |
| Maximum operating temperature LongTerm, Air | | | 93 °C |
| Crystallization peak temperature | | ASTMD3418 | 216 °C |
| | ASTME831 | 9.9E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.