Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.22 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.60 % |
| Shrinkage rate | | ISO 294-4 | 0.15 % |
| Water absorption rate | | ISO 62 | 7.0 % |
| Water absorption rate | | ISO 62 | 2.7 % |
| viscosity number | | ISO 307 | 150 cm³/g |
| hardness | Test Condition | Test Method | Test Result |
|---|
| ball-indentation hardness | | ISO 2039-1 | 170 MPa |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2/1 | 5600 MPa |
| tensile strength | Yield | ISO 527-2/50 | 130 MPa |
| tensile strength | Break | ISO 527-2/5 | 130 MPa |
| Tensile strain | Yield | ISO 527-2/50 | 4.0 % |
| Tensile strain | Break | ISO 527-2/5 | 4.0 % |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 5.0 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 5.5 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 43 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 48 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC 60243-1 | 40 kV/mm |
| relative permittivity | | IEC 60250 | 3.70 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.0E-4到1.3E-4 cm/cm/°C |
| Heat distortion temperature | | ISO 75-2/A | 195 °C |
| Heat distortion temperature | | ISO 75-2/C | 65.0 °C |
| vicat | | ISO 306/B120 | 210 °C |
| melting temperature | | ISO 11357-3 | 220 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 4.0E-5到6.0E-5 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.