PA6 Tarnamid® T-27 GF 15 MW 25 Grupa Azoty ATT Polymers GmbH

Properties:
Filler
glass fiber reinforced material
15%
filler by weight
mineral filler
25%
filler by weight
Usages:
Applications in the fields of electrical appliances
household goods
automobiles
electrical and electronic applications
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ISO 1183	1.40 g/cm³
Shrinkage rate		ISO 294-4	0.001 %
Shrinkage rate	Shrinkage rate		ISO 294-4	0.01 %
Water absorption rate		ISO 62	1.1 %
melt mass-flow rate		ISO 1133	60 cm³/10min

Mechanical properties	Test Method	Test Result
elongation at break	ISO 527-2	3 %
Tensile modulus	ISO 527-2	10700 MPa
bending strength	ISO 178	<=165 MPa
Flexural modulus	ISO 178	9400 MPa
Charpy Notched Impact Strength	ISO 179/1eA	4.5 kJ/m²
Impact strength of simply supported beam without notch	ISO 179/1eU	42 kJ/m²
tensile strength	ISO 527-2	110 MPa

Flame retardant performance	Test Condition	Test Method	Test Result
UL flame retardant rating		UL -94	HB 1.6mm

Thermal performance	Test Condition	Test Method	Test Result
Heat distortion temperature		ISO 75-2/A	195 °C
vicat		ISO 306/B50	210 °C
vicat	vicat	Melting Temperature	ISO 11357-3	221 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.