PA6 Tarnamid® T-27 GF 15 MW 25 Grupa Azoty ATT Polymers GmbH
--
Applications in the fields of electrical appliances, household goods, automobiles, electrical and electronic applications
Filler, glass fiber reinforced material, 15%, filler by weight, mineral filler, 25%, filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T-27 GF 15 MW 25 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 9400 MPa |
| Tensile modulus | 23°C | ISO 527-2 | 10700 MPa |
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.5 kJ/m² |
| tensile strength | 23°C | ISO 527-2 | 110 MPa |
| elongation at break | 23°C | ISO 527-2 | 3 % |
| bending strength | 3.5%弯曲,23°C | ISO 178 | <=165 MPa |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 42 kJ/m² |
| Flame retardant performance | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T-27 GF 15 MW 25 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.6mm |
| physical property | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T-27 GF 15 MW 25 |
|---|---|---|---|
| Water absorption rate | (23°C,24hr) | ISO 62 | 1.1 % |
| Shrinkage rate | TD | ISO 294-4 | 0.01 % |
| MD | ISO 294-4 | 0.001 % | |
| density | ISO 1183 | 1.40 g/cm³ | |
| melt mass-flow rate | 275℃/5Kg | ISO 1133 | 60 cm³/10min |
| Thermal performance | Test Condition | Test Method | Grupa Azoty ATT Polymers GmbH/Tarnamid® T-27 GF 15 MW 25 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/A | 195 °C |
| vicat | 熔融温度 | ISO 11357-3 | 221 °C |
| 干,5.1kg | ISO 306/B50 | 210 °C |