POM HOSTAFORM® LW90FS-K
33
- Properties:wear resistantGood wear resistance
- Usages:Fitness equipmentAutomotive ApplicationsThin walled products
Compare
View PricesTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Shrinkage rate | ISO294-4 | 1.1 % | |
| ISO294-4 | 0.90 % | ||
| density | ISO1183 | 1.51 g/cm³ | |
| Melt volume flow rate | ISO1133 | 8.00 cm3/10min |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile strain | ISO527-2/1A/50 | 17 % | |
| Tensile modulus | ISO527-2/1A/1 | 2100 Mpa | |
| Tensile stress | ISO527-2/1A/50 | 44.0 Mpa | |
| Flexural modulus | ISO178 | 2050 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Impact strength of cantilever beam gap | ISO180/1A | 4.4 kJ/m² | |
| Impact strength of simply supported beam without notch | ISO179/1eU | 61 kJ/m² | |
| Charpy Notched Impact Strength | ISO179/1eA | 4.0 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melting temperature | ISO11357-3 | 166 °C | |
| ISO75-2/A | 87.0 °C | ||
| ISO11359-2 | 1.1E-04 cm/cm/°C | ||
| ISO11359-2 | 1.2E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.