Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM LW90FS-K CELANESE GERMANY
HOSTAFORM®
Fitness equipment、Automotive Applications、Thin walled products
wear resistant、Good wear resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE GERMANY/LW90FS-K |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 61 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 4.4 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CELANESE GERMANY/LW90FS-K |
|---|---|---|---|
| Tensile strain | 屈服 | ISO 527-2/1A/50 | 17 % |
| Tensile modulus | ISO 527-2/1A/1 | 2100 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 2050 Mpa |
| tensile strength | 屈服 | ISO 527-2/1A/50 | 44.0 Mpa |
| physical property | Test Condition | Test Method | CELANESE GERMANY/LW90FS-K |
|---|---|---|---|
| Melt volume flow rate | 190°C/2.16kg | ISO 1133 | 8.00 cm3/10min |
| Shrinkage rate | TD | ISO 294-4 | 1.1 % |
| MD | ISO 294-4 | 0.90 % | |
| density | ISO 1183 | 1.51 g/cm³ |
| Thermal performance | Test Condition | Test Method | CELANESE GERMANY/LW90FS-K |
|---|---|---|---|
| melting temperature | ISO 11357-3 | 166 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 87.0 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| TD | ISO 11359-2 | 1.2E-04 cm/cm/°C |