PA+PP Latiblend 6252 H2 G/30
0
- Properties:Mechanical properties
CompareTechnical Data Sheet
| Test Condition | Test Method | Test Result | |
|---|---|---|---|
| Tensile strain | ISO 527-2/5 | 7.5 % | |
| Charpy Notched Impact Strength | ISO 179/1eA | 8.0 kJ/m² | |
| ISO 179/1eA | 10 kJ/m² | ||
| Impact strength of simply supported beam without notch | ISO 179/1eU | 55 kJ/m² | |
| tensile strength | ISO 527-2/5 | 55.0 MPa | |
| ISO 527-2/5 | 40.0 MPa | ||
| ISO 527-2/5 | 30.0 MPa | ||
| ISO 527-2/5 | 125 MPa | ||
| ISO 527-2/5 | 80.0 MPa | ||
| Water absorption rate | ISO 62 | 0.27 % | |
| Tensile modulus | ISO 527-2/1 | 9400 MPa | |
| ISO 527-2/1 | 6400 MPa | ||
| ISO 527-2/1 | 4700 MPa | ||
| ISO 527-2/1 | 3100 MPa | ||
| ISO 527-2/1 | 2100 MPa | ||
| tensile strength | ISO 527-2/5 | 80.0 MPa | |
| Impact strength of simply supported beam without notch | ISO 179/1eU | 55 kJ/m² | |
| Heat distortion temperature | ISO 75-2/B | 195 °C | |
| ISO 75-2/A | 160 °C | ||
| Continuous use temperature | 120 °C | ||
| vicat | ISO 306/B50 | 170 °C | |
| Linear coefficient of thermal expansion | ISO 11359-2 | 8E-06 cm/cm/°C | |
| UL flame retardant rating | UL 94 | HB | |
| Shrinkage rate | ISO 294-4 | 0.80to1.1 % | |
| ISO 294-4 | 0.35to0.50 % | ||
| Tensile strain | ISO 527-2/5 | 6.0 % | |
| ISO 527-2/5 | 6.8 % | ||
| ISO 527-2/5 | 2.7 % | ||
| ISO 527-2/5 | 4.6 % | ||
| ISO 527-2/5 | 6.0 % | ||
| ISO 527-2/5 | 6.7 % | ||
| tensile strength | ISO 527-2/5 | 55.0 MPa | |
| ISO 527-2/5 | 40.0 MPa | ||
| ISO 527-2/5 | 25.0 MPa | ||
| Tensile strain | ISO 527-2/5 | 4.0 % | |
| ISO 527-2/5 | 5.0 % | ||
| density | ISO 1183 | 1.24 g/cm³ |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.