Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA+PP Latiblend 6252 H2 G/30 LATI S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Test Condition | Test Method | LATI S.p.A./Latiblend 6252 H2 G/30 | |
|---|---|---|---|
| Water absorption rate | 23°C,24hr | ISO 62 | 0.27 % |
| Tensile modulus | 120°C | ISO 527-2/1 | 3100 MPa |
| Continuous use temperature | 120 °C | ||
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.80to1.1 % |
| Tensile strain | 断裂,90°C | ISO 527-2/5 | 6.0 % |
| 断裂,120°C | ISO 527-2/5 | 6.7 % | |
| density | ISO 1183 | 1.24 g/cm³ | |
| Tensile strain | 屈服,150°C | ISO 527-2/5 | 6.8 % |
| vicat | ISO 306/B50 | 170 °C | |
| tensile strength | 屈服,60°C | ISO 527-2/5 | 80.0 MPa |
| Tensile strain | 屈服,60°C | ISO 527-2/5 | 4.0 % |
| tensile strength | 屈服,150°C | ISO 527-2/5 | 30.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.7 % |
| 断裂,60°C | ISO 527-2/5 | 4.6 % | |
| Tensile modulus | 90°C | ISO 527-2/1 | 4700 MPa |
| tensile strength | 断裂,150°C | ISO 527-2/5 | 25.0 MPa |
| 断裂,23°C | ISO 527-2/5 | 125 MPa | |
| 断裂,60°C | ISO 527-2/5 | 80.0 MPa | |
| Tensile modulus | 150°C | ISO 527-2/1 | 2100 MPa |
| Impact strength of simply supported beam without notch | -20°C | ISO 179/1eU | 55 kJ/m² |
| Charpy Notched Impact Strength | -20°C | ISO 179/1eA | 8.0 kJ/m² |
| 23°C | ISO 179/1eA | 10 kJ/m² | |
| Tensile strain | 断裂,150°C | ISO 527-2/5 | 7.5 % |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 55 kJ/m² |
| Tensile strain | 屈服,90°C | ISO 527-2/5 | 5.0 % |
| UL flame retardant rating | 0.75mm | UL 94 | HB |
| Tensile strain | 屈服,120°C | ISO 527-2/5 | 6.0 % |
| tensile strength | 断裂,120°C | ISO 527-2/5 | 40.0 MPa |
| Linear coefficient of thermal expansion | MD：30到100°C | ISO 11359-2 | 8E-06 cm/cm/°C |
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.35to0.50 % |
| Tensile modulus | 60°C | ISO 527-2/1 | 6400 MPa |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 195 °C |
| Tensile modulus | 23°C | ISO 527-2/1 | 9400 MPa |
| tensile strength | 屈服,90°C | ISO 527-2/5 | 55.0 MPa |
| 断裂,90°C | ISO 527-2/5 | 55.0 MPa | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 160 °C |
| tensile strength | 屈服,120°C | ISO 527-2/5 | 40.0 MPa |