Technical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|
| 熔融体积流量 | 260°C/2.16 kg | ISO 1133 | 20 cm³/10 min |
| 熔体质量流动速率 | 260°C/2.16 kg | ISO 1133 | 21 |
| 收缩率 2 | ASTM D 955 | | 0.4~0.6 % |
| 熔体体积流动速率(MVR) | 260°C/2.16 kg | ISO 1133 | 20 cm³/10 min |
| 熔体质量流动速率(MFR) | 260°C/2.16 kg | ASTM D1238 | 21 g/10min |
| 热学性能 | Test Condition | Test Method | Test Result |
|---|
| 维卡软化温度(Vicat) | 1KG,50℃/ | ASTM D1525 | 107 °C |
| 维卡软化温度(Vicat) | 5KG,50℃ | ASTM D1525 | 101 °C |
| 维卡软化温度(Vicat) | 1KG,50℃ | ISO 306 | 107 °C |
| 维卡软化温度(Vicat) | 5KG,50℃ | ISO 306 | 101 °C |
| 线性膨胀系数(CLTE)纵向(Flow) | Flow:23-5 | ISO 11359-2 | 80 °C |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|
| 拉伸强度屈服(yld) | 50mm/mi | ASTM D638 | 600 kg/cm2 |
| 拉伸强度屈服(yld) | 50mm/mi | ISO 527 | 60 Mpa |
| 拉伸强度断裂(brk) | 50mm/mi | ISO 527 | 55 Mpa |
| 拉伸延伸率断裂(brk) | 50mm/m | ASTM D638 | 1 |
| 拉伸延伸率断裂(brk) | 50mm/m | ISO 527 | 1.2 |
| 弯曲强度 | 1.3mm/m | ASTM D790 | 900 kg/cm2 |
| 弯曲强度 | 2mm/mi | ISO 178 | 90 Mpa |
| 弯曲模量 | 1.3mm/m | ASTM D790 | 25000 kg/cm2 |
| 弯曲模量 | 2mm/m | ISO 178 | 2500 Mpa |
| 电学性能 | Test Condition | Test Method | Test Result |
|---|
| 体积电阻率 | | IEC 60093 | 390000000000000000 Ohm-m |
| 表面电阻率 | | IEC 60093 | 290000000000000000 Ohm |
| 介电常数 | | IEC 60250 | 3.1 - |
| 硬度 | Test Condition | Test Method | Test Result |
|---|
| 洛氏硬度R | 23℃ | ASTM D785 | 119 R |
| 洛氏硬度R | 23℃ | ISO 2039-2 | 119 R |
| 燃烧性能 | Test Condition | Test Method | Test Result |
|---|
| UL 防火等级V-0 | | UL94 | 1.5 mm |
| UL 防火等级5VB | | UL94 | 2 mm |
| UL 防火等级5VA | | UL94 | 3 mm |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|
| 简支梁缺口(Charpy Notched) | -30℃ (-22℉) | ISO 179 | 12 kJ/m² |
| 简支梁缺口(Charpy Notched) | 23℃ (73℉) | ISO 179 | 40 kJ/m² |
| 悬臂梁缺口(Izod Notched) | -30℃ (-22℉) | ISO 180 | 12 |
| 悬臂梁缺口(Izod Notched) | 23℃ (73℉) | ASTM D256 | 52 |
| 悬臂梁缺口(Izod Notched) | 23℃ (73℉) | ISO 180 | 40 |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.