Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Specific volume | | ASTM D792 | 0.830 cm³/g |
| melt mass-flow rate | | ISO 1133 | 16 g/10 min |
| Molten Volume Flow Rate (MVR) | | ISO 1133 | 15.0 cm3/10min |
| Shrinkage rate | | 内部方法 | 0.80 到 1.0 % |
| Shrinkage rate | | 内部方法 | 0.80 到 1.0 % |
| Water absorption rate | | ISO 62 | 0.50 % |
| Water absorption rate | | ISO 62 | 0.15 % |
| Outdoor applicability | | UL 746C | f2 |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ASTM D638 | 2250 Mpa |
| Tensile modulus | | ASTM D638 | 2250 Mpa |
| Tensile modulus | | ISO 527-2/1 | 2050 Mpa |
| tensile strength | | ASTM D638 | 53.0 Mpa |
| tensile strength | | ISO 527-2/50 | 50.0 Mpa |
| tensile strength | | ASTM D638 | 51.0 Mpa |
| tensile strength | | ISO 527-2/50 | 50.0 Mpa |
| elongation | | ASTM D638 | 4.0 % |
| elongation | | ISO 527-2/50 | 4.0 % |
| elongation | | ASTM D638 | 120 % |
| elongation | | ISO 527-2/50 | 120 % |
| Flexural modulus | | ASTM D790 | 2030 Mpa |
| Flexural modulus | | ISO 178 | 2000 Mpa |
| Bending stress | | ISO 178 | 80.0 Mpa |
| Bending stress | | ASTM D790 | 84.0 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Dart impact equipped with measuring instruments | | ASTM D3763 | 60.0 J |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Arc resistance 12 | | ASTM D495 | PLC 5 |
| Compared to the Leakage Tracking Index (CTI) | | UL 746 | PLC 1 |
| High arc combustion index (HAI) | | UL 746 | PLC 0 |
| High Voltage Arc Traceability Rate (HVTR) | | UL 746 | PLC 0 |
| Hot wire ignition (HWI) | | UL 746 | PLC 3 |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 110 °C |
| drying time | | | 4.0 到 6.0 hr |
| Suggested maximum moisture content | | | 0.020 % |
| Suggested injection volume | | | 50 到 80 % |
| Temperature at the rear of the barrel | | | 245 到 265 °C |
| Temperature in the middle of the barrel | | | 250 到 270 °C |
| Temperature at the front of the material cylinder | | | 255 到 275 °C |
| Spray nozzle temperature | | | 255 到 270 °C |
| Processing (melt) temperature | | | 260 到 275 °C |
| Temperature | | | 65 到 90 °C |
| Back pressure | | | 0.300 到 0.700 Mpa |
| screw speed | | | 50 到 80 rpm |
| Exhaust hole depth | | | 0.013 到 0.020 mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Thermal deformation temperature under load | | ASTM D648 | 107 °C |
| Thermal deformation temperature under load | | ASTM D648 | 84.0 °C |
| Thermal deformation temperature under load | | ASTM D648 | 99.0 °C |
| Thermal deformation temperature under load | | ISO 75-2/Af | 75.0 °C |
| vicat | | ASTM D152511 | 122 °C |
| vicat | | ISO 306/B50 | 120 °C |
| vicat | | ISO 306/B120 | 125 °C |
| | ASTM E831, ISO 11359-2 | 9.5E-5 cm/cm/°C |
| | ASTM E831 | 9.0E-5 cm/cm/°C |
| | ISO 11359-2 | 9.0E-5 cm/cm/°C |
| RTI Elec | | UL 746 | 75.0 °C |
| RTI Imp | | UL 746 | 75.0 °C |
| RTI | | UL 746 | 75.0 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.