PBT/PC 5220U-BK1066 SABIC INNOVATIVE SHANGHAI
XENOY™
Plastic bag、chip、Electrical appliances
Antichemical、Low temperature impact re
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/5220U-BK1066 |
|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 60.0 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/5220U-BK1066 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 50.0 Mpa |
| Bending stress | -- 7, 8 | ISO 178 | 80.0 Mpa |
| Flexural modulus | -- 7 | ISO 178 | 2000 Mpa |
| elongation | 断裂 | ISO 527-2/50 | 120 % |
| 屈服 5 | ASTM D638 | 4.0 % | |
| Bending stress | 屈服, 50.0 mm 跨距 6 | ASTM D790 | 84.0 Mpa |
| Tensile modulus | -- 3 | ASTM D638 | 2250 Mpa |
| -- 4 | ASTM D638 | 2250 Mpa | |
| tensile strength | 屈服 5 | ASTM D638 | 53.0 Mpa |
| 断裂 | ISO 527-2/50 | 50.0 Mpa | |
| elongation | 屈服 | ISO 527-2/50 | 4.0 % |
| Flexural modulus | 50.0 mm 跨距 6 | ASTM D790 | 2030 Mpa |
| tensile strength | 断裂 5 | ASTM D638 | 51.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 2050 Mpa |
| elongation | 断裂 5 | ASTM D638 | 120 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/5220U-BK1066 |
|---|---|---|---|
| Hot wire ignition (HWI) | UL 746 | PLC 3 | |
| Arc resistance 12 | ASTM D495 | PLC 5 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 0 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 1 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/5220U-BK1066 |
|---|---|---|---|
| UL flame retardant rating | 1.5 mm | UL 94 | HB |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/5220U-BK1066 |
|---|---|---|---|
| melt mass-flow rate | 250°C/5.0 kg | ISO 1133 | 16 g/10 min |
| Shrinkage rate | 横向流动 2 | 内部方法 | 0.80 到 1.0 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.15 % |
| Outdoor applicability | UL 746C | f2 | |
| Molten Volume Flow Rate (MVR) | 250°C/5.0 kg | ISO 1133 | 15.0 cm3/10min |
| Specific volume | ASTM D792 | 0.830 cm³/g | |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.80 到 1.0 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.50 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/5220U-BK1066 |
|---|---|---|---|
| vicat | -- | ASTM D152511 | 122 °C |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 6.40 mm | ASTM D648 | 99.0 °C |
| RTI | UL 746 | 75.0 °C | |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 10 | ISO 75-2/Af | 75.0 °C |
| vicat | -- | ISO 306/B120 | 125 °C |
| 横向 : -40 到 40°C | ASTM E831 | 9.0E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 6.40 mm | ASTM D648 | 107 °C |
| 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 84.0 °C | |
| vicat | -- | ISO 306/B50 | 120 °C |
| 横向 : -40°C | ISO 11359-2 | 9.0E-5 cm/cm/°C | |
| 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 9.5E-5 cm/cm/°C | |
| RTI Imp | UL 746 | 75.0 °C | |
| RTI Elec | UL 746 | 75.0 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE SHANGHAI/5220U-BK1066 |
|---|---|---|---|
| Processing (melt) temperature | 260 到 275 °C | ||
| drying temperature | 110 °C | ||
| Exhaust hole depth | 0.013 到 0.020 mm | ||
| Temperature at the front of the material cylinder | 255 到 275 °C | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 250 到 270 °C | ||
| Temperature | 65 到 90 °C | ||
| screw speed | 50 到 80 rpm | ||
| Temperature at the rear of the barrel | 245 到 265 °C | ||
| Back pressure | 0.300 到 0.700 Mpa | ||
| drying time | 4.0 到 6.0 hr | ||
| Suggested injection volume | 50 到 80 % | ||
| Spray nozzle temperature | 255 到 270 °C |