PBT+ASA SCHULADUR® A3 GF 20 A SCHULMAN USA
0
- Properties:Fillerglass fiber reinforced material20%filler by weight
CompareTechnical Data Sheet
| 物理性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 密度 | ISO1183/A | 1.34 g/cm³ | |
| 熔体体积流动速率 | 250°C/2.16kg | ISO1133 | 20.0 cm³/10min |
| 机械性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 拉伸模量 | ISO527-2/1A/1 | 6500 MPa | |
| 拉伸应力 | Break | ISO527-2/1A/5 | 96.0 MPa |
| 拉伸应变 | Break | ISO527-2/1A/5 | 2.6 % |
| 可燃性 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 燃烧速率 | 2.00mm | ISO3795 | 20 mm/min |
| 可燃性等级 | 1.5mm | IEC60695-11-10,-20 | HB |
| 3.0mm | IEC60695-11-10,-20 | HB | |
| 灼热丝易燃指数 | 1.5mm | IEC60695-2-12 | 700 °C |
| 3.0mm | IEC60695-2-12 | 700 °C | |
| 热灯丝点火温度 | 1.5mm | IEC60695-2-13 | 725 °C |
| 3.0mm | IEC60695-2-13 | 725 °C |
| 电气性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 漏电起痕指数 | 解决方案A | IEC60112 | 250 V |
| 冲击性能 | Test Condition | Test Method | Test Result |
|---|---|---|---|
| 热变形温度 | 0.45MPa,未退火 | ISO75-2/Bf | 210 °C |
| 1.8MPa,未退火 | ISO75-2/Af | 172 °C | |
| 维卡软化温度 | -- | ISO306/A50 | 205 °C |
| -- | ISO306/B50 | 145 °C | |
| 简支梁缺口冲击强度 | -30°C | ISO179/1eA | 4.5 kJ/m² |
| 23°C | ISO179/1eA | 7.5 kJ/m² | |
| 简支梁无缺口冲击强度 | -30°C | ISO179/1eU | 30 kJ/m² |
| 23°C | ISO179/1eU | 45 kJ/m² |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.