PBT+ASA SCHULADUR® A3 GF 20 A SCHULMAN USA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodA SCHULMAN USA/SCHULADUR® A3 GF 20
Charpy Notched Impact Strength23°CISO 179/1eA7.5 kJ/m²
-30°CISO 179/1eA4.5 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU45 kJ/m²
-30°CISO 179/1eU30 kJ/m²
Electrical performanceTest ConditionTest MethodA SCHULMAN USA/SCHULADUR® A3 GF 20
Compared to the Leakage Tracking Index (CTI)解决方案AIEC 60112PLC 2
Mechanical propertiesTest ConditionTest MethodA SCHULMAN USA/SCHULADUR® A3 GF 20
Tensile modulusISO 527-2/1A/16500 MPa
tensile strength 断裂ISO 527-2/1A/596.0 MPa
Tensile strain断裂ISO 527-2/1A/52.6 %
flammabilityTest ConditionTest MethodA SCHULMAN USA/SCHULADUR® A3 GF 20
Burning wire flammability index3.0mmIEC 60695-2-12700 °C
1.5mmIEC 60695-2-12700 °C
Hot filament ignition temperature3.0mmIEC 60695-2-13725 °C
burning rate2.00mmISO 379520 mm/min
Flammability level3.0mmIEC 60695-11-10,-20HB
1.5mmIEC 60695-11-10,-20HB
Hot filament ignition temperature1.5mmIEC 60695-2-13725 °C
physical property Test ConditionTest MethodA SCHULMAN USA/SCHULADUR® A3 GF 20
densityISO 1183/A1.34 g/cm³
Melt volume flow rate250°C/2.16kgISO 113320.0 cm³/10min
Thermal performanceTest ConditionTest MethodA SCHULMAN USA/SCHULADUR® A3 GF 20
Heat distortion temperature1.8MPa,未退火，HDTISO 75-2/Af172 °C
vicat--ISO 306/A50205 °C
--ISO 306/B50145 °C
Heat distortion temperature0.45MPa,未退火，HDTISO 75-2/Bf210 °C