HDPE PRE-ELEC® PE 1202

Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
density		ASTM D792	1.08 g/cm³
density	density		ISO 1183	1.09 g/cm³
melt mass-flow rate		ISO 1133	2.0 g/10min
Shrinkage rate		ASTM D955	1.5to2.5 %
Shrinkage rate	Shrinkage rate		ISO 294-4	1.5to2.5 %

hardness	Test Condition	Test Method	Test Result
Shore hardness		ISO 868	66
Shore hardness	Shore hardness	Shore A	ISO 868	95

Impact resistance	Test Condition	Test Method	Test Result
Impact strength of cantilever beam gap		ISO 180	18 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ISO 180	43 kJ/m²
Suspended wall beam without notch impact strength		ASTM D256	NoBreak
	Suspended wall beam without notch impact strength		ASTM D256	NoBreak
		Suspended wall beam without notch impact strength		ISO 180	NoBreak
		Suspended wall beam without notch impact strength	Suspended wall beam without notch impact strength		ISO 180	NoBreak
Charpy Notched Impact Strength		ASTM D256	23 kJ/m²
Impact strength of simply supported beam without notch		ASTM D256	NoBreak
Impact strength of cantilever beam gap		ASTM D256	16.8 kJ/m²
Impact strength of cantilever beam gap	Impact strength of cantilever beam gap		ASTM D256	44.1 kJ/m²
Charpy Notched Impact Strength		ISO 179	24 kJ/m²
	Charpy Notched Impact Strength		ISO 179	36 kJ/m²
	Charpy Notched Impact Strength	Charpy Notched Impact Strength		ASTM D256	36 kJ/m²
Impact strength of simply supported beam without notch		ASTM D256	NoBreak
	Impact strength of simply supported beam without notch		ISO 179	NoBreak
	Impact strength of simply supported beam without notch	Impact strength of simply supported beam without notch		ISO 179	NoBreak

Mechanical properties	Test Condition	Test Method	Test Result
Tensile strain		ISO 527-2	30 %
Flexural modulus		ASTM D790	1200 MPa
Flexural modulus	Flexural modulus		ISO 178	1200 MPa
Tensile strain	Yield	ISO 527-2	10 %
tensile strength		ASTM D638	13.1 MPa
	tensile strength	Yield	ASTM D638	26.9 MPa
		tensile strength	Yield	ISO 527-2	31.0 MPa
		tensile strength	tensile strength		ISO 527-2	13.0 MPa

Electrical performance	Test Condition	Test Method	Test Result
Surface Resistivity		IEC 61340-2-3	<1.0E+5 ohms
Volume resistivity		内部方法	<1.0E+4 ohms·cm

Thermal performance	Test Condition	Test Method	Test Result
vicat		ASTM D15253	128 °C
	vicat		ASTM D15254	81.1 °C
		vicat		ISO 306/A50	128 °C
		vicat	vicat		ISO 306/B50	81.0 °C
Heat distortion temperature		ASTM D648B	83.9 °C
	Heat distortion temperature		ISO 75-2/Bf	84.0 °C
		Heat distortion temperature		ASTM D648A	87.2 °C
		Heat distortion temperature	Heat distortion temperature		ISO 75-2/Af	87.0 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.