Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | 内部方法 | <1.40 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.50到0.80 % |
| Water absorption rate | | 内部方法 | <40.0 mg |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| %1 - %2 | | | 60.0 s/mm |
| CompressionMoldingPressure | | | 25.0到35.0 MPa |
| CompressionMoldingPreheatTemperature | | | 80到120 °C |
| CompressionMoldingPreheatTime | | | 5.0到15.0 min |
| CompressionMoldingTemperature | | | 160到180 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Bending stress | | 内部方法 | >80.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | 内部方法 | >1.7 kJ/m² |
| Impact strength of simply supported beam without notch | | 内部方法 | >4.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Dissipation Factor | | 内部方法 | <0.050 |
| Surface Resistivity | | 内部方法 | >1.0E+11 ohms |
| Volume resistivity | | 内部方法 | >1.0E+12 ohms·cm |
| dielectric strength | | 内部方法 | >10 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | 内部方法 | >160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.