Phenolic Taizhou Phenolic PF2A2-141 Taizhou Changxiong Plastic Co., Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Taizhou Changxiong Plastic Co., Ltd./Taizhou Phenolic PF2A2-141 |
|---|---|---|---|
| Charpy Notched Impact Strength | 内部方法 | >1.7 kJ/m² | |
| Impact strength of simply supported beam without notch | 内部方法 | >4.5 kJ/m² |
| Supplementary Information | Test Condition | Test Method | Taizhou Changxiong Plastic Co., Ltd./Taizhou Phenolic PF2A2-141 |
|---|---|---|---|
| Compression molding pressure | 25.0to35.0 MPa | ||
| %1 - %2 | 60.0 s/mm | ||
| Compression molding temperature | 160to180 °C | ||
| CompressionMoldingPreheatTime | 5.0to15.0 min | ||
| CompressionMoldingPreheatTemperature | 80to120 °C |
| Electrical performance | Test Condition | Test Method | Taizhou Changxiong Plastic Co., Ltd./Taizhou Phenolic PF2A2-141 |
|---|---|---|---|
| dielectric strength | 内部方法 | >10 kV/mm | |
| Dissipation Factor | 内部方法 | <0.050 | |
| Surface Resistivity | 内部方法 | >1.0E+11 ohms | |
| Volume resistivity | 内部方法 | >1.0E+12 ohms·cm |
| Mechanical properties | Test Condition | Test Method | Taizhou Changxiong Plastic Co., Ltd./Taizhou Phenolic PF2A2-141 |
|---|---|---|---|
| bending strength | 内部方法 | >80.0 MPa |
| physical property | Test Condition | Test Method | Taizhou Changxiong Plastic Co., Ltd./Taizhou Phenolic PF2A2-141 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | 0.50to0.80 % | |
| Water absorption rate | 内部方法 | <40.0 mg | |
| density | 内部方法 | <1.40 g/cm³ |
| Thermal performance | Test Condition | Test Method | Taizhou Changxiong Plastic Co., Ltd./Taizhou Phenolic PF2A2-141 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | 内部方法 | >160 °C |