Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.80 g/cm³ |
| Water absorption rate | | ISO 62 | <0.30 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | HB |
| Limiting Oxygen Index | | ISO 4589-2 | 22 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| bending strength | Compression Molded | ISO 178 | 145 MPa |
| Tensile modulus | Compression Molded | ISO 527-2 | 11000 MPa |
| tensile strength | | ISO 527-2 | 60.0 MPa |
| Flexural modulus | Compression Molded | ISO 178 | 9000 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO 179 | 65 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC 60093 | 1E+13 ohms |
| Volume resistivity | | IEC 60093 | 1E+16 ohms·cm |
| dielectric strength | | IEC 60243-1 | 36 kV/mm |
| Dissipation Factor | | IEC 60250 | 0.010 |
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 0 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/A | >200 °C |
| Continuous use temperature | | 内部方法 | 165 °C |
| Glass Transition Temperature | | DSC | 170 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 1.2E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.