Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO1183 | 1.95到2.15 g/cm³ |
| Apparent density | | ISO60 | 0.80到1.00 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.20到0.30 % |
| Water absorption rate | | ISO62 | <0.50 % |
| PostShrinkage | | ISO2577 | <0.10 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | HB |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >10.0 MPa |
| CompressionMoldingTemperature | | | 165到180 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Compression Molded | ISO527-2 | 9000到11000 MPa |
| Tensile stress | | ISO527-2 | 35.0到60.0 MPa |
| Flexural modulus | Compression Molded | ISO178 | 12000到15000 MPa |
| Bending stress | Compression Molded | ISO178 | 85.0到130 MPa |
| compression stress | | ISO604 | 150到200 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Compression Molded | ISO179/1eA | 2.5到3.5 kJ/m² |
| Impact strength of simply supported beam without notch | Compression Molded | ISO179/1eU | 4.0到6.0 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | IEC60243-1 | 25到35 kV/mm |
| | IEC60250 | 5.006.00 |
| | IEC60250 | 4.005.00 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| Dissipation Factor | | IEC60250 | 0.010到0.030 |
| arc resistance | | ASTMD495 | PLC 4 |
| CTI | | IEC60112 | >600 V |
| Surface Resistivity | | IEC60093 | 1.0E+11到1.0E+12 ohms |
| Volume resistivity | | IEC60093 | >1.0E+13 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/C | 180到200 °C |
| | ISO11359-2 | 1.0E-5到2.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.60到0.70 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare