| Impact resistance | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 5000 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 模压成型 | ISO 179/1eU | 4.0to6.0 kJ/m² |
| Charpy Notched Impact Strength | 模压成型 | ISO 179/1eA | 2.5to3.5 kJ/m² |
| Supplementary Information | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 5000 |
|---|---|---|---|
| Compression molding pressure | >10.0 MPa | ||
| Compression molding temperature | 165to180 °C |
| Mechanical properties | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 5000 |
|---|---|---|---|
| tensile strength | CompressionMolded | ISO 527-2 | 35.0to60.0 MPa |
| compression stress | ISO 604 | 150to200 MPa | |
| Tensile modulus | 模压成型 | ISO 527-2 | 9000to11000 MPa |
| Flexural modulus | 模压成型 | ISO 178 | 12000to15000 MPa |
| bending strength | 模压成型 | ISO 178 | 85.0to130 MPa |
| Electrical performance | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 5000 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| dielectric strength | IEC 60243-1 | 25to35 kV/mm | |
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm | |
| relative permittivity | 100Hz | IEC 60250 | 5.006.00 |
| Dissipation Factor | 100Hz | IEC 60250 | 0.010to0.030 |
| arc resistance | ASTM D495 | PLC 4 | |
| relative permittivity | 1MHz | IEC 60250 | 4.005.00 |
| Surface Resistivity | IEC 60093 | 1.0E+11到1.0E+12 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.010to0.030 |
| flammability | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 5000 |
|---|---|---|---|
| UL flame retardant rating | 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 5000 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | <0.10 % | |
| Apparent density | ISO 60 | 0.80to1.00 g/cm³ | |
| Water absorption rate | 23°C,24hr | ISO 62 | <0.50 % |
| Shrinkage rate | MD2 | ISO 2577 | 0.20to0.30 % |
| density | ISO 1183 | 1.95to2.15 g/cm³ |
| Thermal performance | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 5000 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：50到100°C | ISO 11359-2 | 1.0E-5到2.0E-5 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 180to200 °C |
| thermal conductivity | ASTME1461 | 0.60to0.70 W/m/K |