PP SABIC® 7705-00900
68
- Usages:Automotive sector
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| melt mass-flow rate | ISO1133 | 22 g/10min |
| hardness | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ISO868 | 60 |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| NotchedIzodImpact8 | ASTMD256 | 120 J/m | |
| Suspended wall beam notch impact strength 6 | ISO180/1A | 3.0 kJ/m² | |
| ISO180/1A | 6.0 kJ/m² | ||
| ISO180/1A | 20 kJ/m² | ||
| Cantilever beam without notch impact strength 8 | ASTMD4812 | NoBreak | |
| Dart impact equipped with measuring instruments 9 | ASTMD3763 | 7.10 J | |
| ASTMD3763 | 19.1 J | ||
| ASTMD3763 | 22.1 J |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile stress | ISO527-2/50 | 22.0 Mpa | |
| tensile strength | ASTMD638 | 16.0 Mpa | |
| Tensile stress | ISO527-2/1A/50 | 17.0 Mpa | |
| elongation | ASTMD638 | 4.6 % | |
| Tensile strain | ISO527-2/50 | 4.4 % | |
| elongation | ASTMD638 | 24 % | |
| Tensile strain | ISO527-2/50 | 32 % | |
| Flexural modulus | ISO178 | 2080 Mpa | |
| ASTMD790 | 1900 Mpa | ||
| Tensile modulus | ASTMD638 | 1910 Mpa | |
| ISO527-2/1 | 2010 Mpa | ||
| tensile strength | ASTMD638 | 23.0 Mpa |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| ASTMD648 | 112 °C | ||
| Hot deformation temperature 6 | ISO75-2/B | 105 °C | |
| ASTMD648 | 57.0 °C | ||
| Hot deformation temperature 6 | ISO75-2/A | 59.0 °C | |
| vicat | ISO306/A50 | 130 °C | |
| ISO11359-2 | 5.9E-05 cm/cm/°C | ||
| ISO11359-2 | 1.5E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.