Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.19 g/cm³ |
| Melt volume flow rate | | ISO 1133 | 20.0 cm³/10min |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| Haze ratio | | ISO 13468 | 82 % |
| transmissivity | | ISO 13468 | 87.0 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL 94 | V-2 |
| Burning wire flammability index | | IEC 60695-2-12 | 850 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 850 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 850960 °C |
| Burning wire flammability index | | IEC 60695-2-12 | 850960 °C |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| half-power angle | | | 3.00 ° |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | | ISO 527-2 | 2500 MPa |
| tensile strength | Yield | ISO 527-2 | 64.0 MPa |
| tensile strength | | ISO 527-2 | 64.0 MPa |
| Tensile strain | Yield | ISO 527-2 | 6.0 % |
| Tensile strain | Break | ISO 527-2 | 85 % |
| Flexural modulus | | ISO 178 | 2400 MPa |
| bending strength | | ISO 178 | 74.0 MPa |
| bending strength | | ISO 178 | 97.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 无断裂 |
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 10 kJ/m² |
| Charpy Notched Impact Strength | | ISO 179/1eA | 11 kJ/m² |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| vicat | | ISO 306/B50 | 143 °C |
| Heat distortion temperature | | ISO 75-2/A | 128 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.