Technical Data Sheet
physical property | Test Condition | Test Method | Test Result |
---|
Shrinkage rate | | ASTM D995 | 0.20 % |
Shrinkage rate | | ASTM D995 | 0.40 % |
density | | ASTM D792 | 1.94 g/cm³ |
hardness | Test Condition | Test Method | Test Result |
---|
Rockwell hardness | | ASTM D785 | 101 M(Scale) |
Rockwell hardness | | ASTM D785 | 119 R |
Other performance | Test Condition | Test Method | Test Result |
---|
Linear coefficient of thermal expansion | | | 1E-03 cm/cm/°C |
Linear coefficient of thermal expansion | | | 1.5E-03 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTME831 | 3E-03 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTME831 | 7E-03 cm/cm/°C |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
tensile strength | | ASTM D638 | 159 Mpa |
elongation at break | | ASTM D638 | 1.1 % |
elongation at break | | ASTME132 | 0.34 |
bending strength | | ASTM D790 | 241 Mpa |
Flexural modulus | | ASTM D790 | 19300 Mpa |
Impact strength of cantilever beam gap | | ASTM D256 | 75 J/m |
Suspended wall beam without notch impact strength | | ASTM D256 | 320 J/m |
Suspended wall beam without notch impact strength | | ASTM D695 | 295 Mpa |
Flame retardant performance | Test Condition | Test Method | Test Result |
---|
UL flame retardant rating | | UL -94 | V-0 0.71mm |
UL flame retardant rating | | UL -94 | V-0.5VA 1.50mm |
UL flame retardant rating | | UL -94 | V-0 3.00mm |
UL flame retardant rating | | UL -94 | V-0 6.00mm |
Limiting Oxygen Index | | ASTM2863 | 65 % |
Electrical performance | Test Condition | Test Method | Test Result |
---|
Dissipation Factor | | ASTM D150 | 2E-03 |
Dissipation Factor | | ASTM D150 | 3E-03 |
Dissipation Factor | | ASTM D495 | 180 S |
Dissipation Factor | | ASTM D3638 | 225 V |
Volume resistivity | | ASTM D257 | 1E+15 Ω.cm |
Surface Resistivity | | ASTM D257 | 1E+16 Ω.cm |
dielectric strength | | ASTM D149 | 10 KV/mm |
dielectric constant | | ASTM D150 | 4.7 1kHz |
dielectric constant | | ASTM D150 | 4.6 1MHz |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ASTM D648 | 265 °C |
Heat distortion temperature | | | 220-240 °C |
Heat distortion temperature | | ASTMC177 | 0.510 W/m/K |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.