Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | ISO62 | <0.55 % |
| PostShrinkage | | ISO2577 | <0.10 % |
| density | | ISO1183 | 1.90到2.10 g/cm³ |
| Apparent density | | ISO60 | 0.75到1.00 g/cm³ |
| Shrinkage rate | | ISO2577 | 0.60到0.90 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| UL flame retardant rating | | UL94 | V-0 |
| Supplementary Information | Test Condition | Test Method | Test Result |
|---|
| CompressionMoldingPressure | | | >10.0 MPa |
| CompressionMoldingTemperature | | | 165到180 °C |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile modulus | Injection | ISO527-2 | 10000到12000 MPa |
| Tensile stress | Injection | ISO527-2 | 40.0到70.0 MPa |
| Flexural modulus | Injection | ISO178 | 14000到16000 MPa |
| Bending stress | Injection | ISO178 | 90.0到120 MPa |
| compression stress | | ISO604 | 150到200 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | Injection | ISO179/1eA | 2.0到4.0 kJ/m² |
| Impact strength of simply supported beam without notch | Injection | ISO179/1eU | 5.0到10 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | IEC60093 | 1.0E+12到1.0E+13 ohms |
| Volume resistivity | | IEC60093 | 1.0E+13到1.0E+14 ohms·cm |
| arc resistance | | ASTMD495 | PLC 4 |
| CTI | | IEC60112 | 600 V |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| | ISO75-2/C | 70.0到130 °C |
| | ISO11359-2 | 1.0E-5到2.0E-5 cm/cm/°C |
| thermal conductivity | | ASTME1461 | 0.50到0.60 W/m/K |
| maximum service temperature | | IEC60216 | 200 °C |
| maximum service temperature | | IEC60216 | 150 °C |
| | ISO75-2/A | 140到170 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.