Polyester, TS RALUPOL® UP 8602 RASCHIG GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 8602 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 注塑 | ISO 179/1eU | 5.0to10 kJ/m² |
| Charpy Notched Impact Strength | 注塑 | ISO 179/1eA | 2.0to4.0 kJ/m² |
| Supplementary Information | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 8602 |
|---|---|---|---|
| Compression molding pressure | >10.0 MPa | ||
| Compression molding temperature | 165to180 °C |
| Electrical performance | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 8602 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 0 | |
| Volume resistivity | IEC 60093 | 1.0E+13到1.0E+14 ohms·cm | |
| arc resistance | ASTM D495 | PLC 4 | |
| Surface Resistivity | IEC 60093 | 1.0E+12到1.0E+13 ohms |
| Mechanical properties | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 8602 |
|---|---|---|---|
| bending strength | 注塑 | ISO 178 | 90.0to120 MPa |
| Flexural modulus | 注塑 | ISO 178 | 14000to16000 MPa |
| compression stress | ISO 604 | 150to200 MPa | |
| tensile strength | 注塑 | ISO 527-2 | 40.0to70.0 MPa |
| Tensile modulus | 注塑 | ISO 527-2 | 10000to12000 MPa |
| flammability | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 8602 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 8602 |
|---|---|---|---|
| Shrinkage rate | ISO 2577 | <0.10 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | <0.55 % |
| Apparent density | ISO 60 | 0.75to1.00 g/cm³ | |
| Shrinkage rate | MD2 | ISO 2577 | 0.60to0.90 % |
| density | ISO 1183 | 1.90to2.10 g/cm³ |
| Thermal performance | Test Condition | Test Method | RASCHIG GmbH/RALUPOL® UP 8602 |
|---|---|---|---|
| maximum service temperature | 20,000h | IEC 60216 | 150 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 140to170 °C |
| Linear coefficient of thermal expansion | MD：50到100°C | ISO 11359-2 | 1.0E-5到2.0E-5 cm/cm/°C |
| Heat distortion temperature | 8.0MPa,未退火，HDT | ISO 75-2/C | 70.0to130 °C |
| thermal conductivity | ASTME1461 | 0.50to0.60 W/m/K | |
| maximum service temperature | <50h | IEC 60216 | 200 °C |