PC TARFLON™ AZ1900-V0 BK IDEMITSU JAPAN

Properties:
Low viscosity
Flame retardant
Usages:
Electrical applications
Casters
Thin walled products
Certificates:
UL
Compare
View Prices

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Molten Volume Flow Rate (MVR)		ISO 1133	18.0 cm3/10min
Spiral Flow?3,?4		内部方法	29.0 CM
Shrinkage rate		内部方法	0.50 到 0.70 %
Shrinkage rate	Shrinkage rate		内部方法	0.50 到 0.70 %
Water absorption rate		ISO 62	0.23 %

hardness	Test Condition	Test Method	Test Result
Rockwell hardness		ISO 2039-2	50
Rockwell hardness	Rockwell hardness		ISO 2039-2	120

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	V-0
ISO 9660			>PC<

Mechanical properties	Test Method	Test Result
Tensile stress	ISO 527-2	65.0 Mpa
Nominal tensile fracture strain	ISO 527-2	95 %
Flexural modulus	ISO 178	2300 Mpa
Bending stress	ISO 178	90.0 Mpa

Electrical performance	Test Method	Test Result
dielectric strength	IEC 60243-1	30 KV/mm
dielectric constant	IEC 60250	2.85
Compared to the Leakage Tracking Index (CTI)	UL 746	PLC 2

injection	Test Condition	Test Method	Test Result
drying temperature			120 °C
drying time			5.0 到 8.0 hr
Temperature at the rear of the barrel			260 到 300 °C
Temperature in the middle of the barrel			260 到 300 °C
Temperature at the front of the material cylinder			260 到 300 °C
Temperature			80 到 120 °C

Thermal performance	Test Method	Test Result
	ISO 75-2/A	125 °C
		ISO 11359-2	6.5E-5 cm/cm/°C
RTI Elec	UL 746	80.0 °C
RTI Imp	UL 746	80.0 °C
RTI	UL 746	80.0 °C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

PC TARFLON™ AZ1900-V0 BK IDEMITSU JAPAN

Technical Data Sheet