Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| melt mass-flow rate | | ASTM D1238 | 3.0 g/10min |
| density | | ASTM D792 | 1.04 g/cm³ |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | | ASTM D2240 | 53 |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| gloss | | ASTM D523 | 3 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D638 | 24.8 MPa |
| elongation | | ASTM D638 | 7.0 % |
| elongation | | ASTM D638 | 10 % |
| Flexural modulus | | ASTM D790 | 814 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of cantilever beam gap | | ASTM D256 | 500 J/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Surface Resistivity | | | 1E+14 ohms |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ASTM D648 | 93.3 °C |
| Heat distortion temperature | | ASTM D648 | 81.1 °C |
| vicat | | ASTM D1525 | 105 °C |
| Linear coefficient of thermal expansion | | ASTM D696 | 9.5E-05 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.