Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Water absorption rate | | % | 0.30 -- |
| Water absorption rate | | % | 4.0 -- |
| Shrinkage rate | | % | 0.30-0.70 -- |
| Shrinkage rate | | % | 0.70-1.3 -- |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | | | 116 -- |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | MPa | 85.0 -- |
| tensile strength | | MPa | 55.0 40.0 |
| tensile strength | | MPa | 25.0 -- |
| Tensile strain | | % | 50 |
| Flexural modulus | | MPa | 2300 -- |
| Flexural modulus | | MPa | 2000 900 |
| Flexural modulus | | MPa | 500 -- |
| bending strength | | MPa | 95.0 55.0 |
| compression stress | | MPa | 65.0 -- |
| shear strength | | MPa | 50.0 45.0 |
| Taber abraser | | mg | 4.00 -- |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Impact strength of simply supported beam without notch | | | 无断裂 |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Volume resistivity | | ohms·cm | 1.0E+13-1.0E+14 -- |
| dielectric constant | | | 3.90 -- |
| dielectric constant | | | 3.60 -- |
| dielectric constant | | | 3.10 -- |
| Dissipation Factor | | | 0.040 -- |
| Dissipation Factor | | | 0.040 -- |
| Dissipation Factor | | | 0.020 -- |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | °C | 180 -- |
| melting temperature | | °C | 225 -- |
| Linear coefficient of thermal expansion | | cm/cm/°C | 1.2E-04 -- |
| specific heat | | J/kg/°C | 1900 -- |
| thermal conductivity | | W/m/K | 0.25 -- |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.