ABS

ABS EGP-7 BASF KOREA

Usages:
LiningPipeline componentsHome appliance componentsPipeline system
Compare

Technical Data Sheet

impact performance	Test Condition	Test Method	Test Result
Impact strength of simply supported beam without notch	23°C	ISO 179	无断裂

flammability	Test Condition	Test Method	Test Result
UL flame retardant rating		UL 94	HB

mechanical properties	Test Condition	Test Method	Test Result
bending strength		ISO 178	65.0 Mpa
Bending modulus		ISO 178	2000 Mpa
Tensile strain	Yield,23°C	ISO 527-2	2.9 %
tensile strength	Yield,23°C	ISO 527-2	43.0 Mpa
Tensile modulus		ISO 527-2	2400 Mpa

thermal performance	Test Condition	Test Method	Test Result
Maximum operating temperature			80 °C
thermal conductivity		DIN 52612	0.17 W/m/K
Linear coefficient of thermal expansion	MD	ISO 11359-2	8.0E-5到1.1E-4 cm/cm/°C
Vicat softening temperature	--	ISO 306/B50	100 °C
Vicat softening temperature	Vicat softening temperature	--	ISO 306/A50	107 °C
Hot deformation temperature	1.8MPa,Annealed	ISO 75-2/A	101 °C
Hot deformation temperature	Hot deformation temperature	0.45MPa,Annealed	ISO 75-2/B	103 °C

Physical properties	Test Condition	Test Method	Test Result
Water absorption rate	Saturation,23°C	ISO 62	0.95 %
Water absorption rate	Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.21 %
Shrinkage rate		ISO 294-4	0.40-0.70 %
Melt Volume Flow Rate (MVR)	220°C/10.0kg	ISO 1133	5.00 cm3/10min
Apparent density			0.55to0.65 g/cm³

Electrical performance	Test Condition	Test Method	Test Result
Volume resistivity		IEC 60093	1E+15 ohms·cm

hardness	Test Condition	Test Method	Test Result
Ball Pressure Test		ISO 2039-1	97.0 Mpa

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.