ABS EGP-7 BASF KOREA
--
Lining、Pipeline components、Home appliance components、Pipeline system
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF KOREA/EGP-7 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO179 | 无断裂 |
| hardness | Test Condition | Test Method | BASF KOREA/EGP-7 |
|---|---|---|---|
| ISO2039-1 | 97.0 Mpa |
| Mechanical properties | Test Condition | Test Method | BASF KOREA/EGP-7 |
|---|---|---|---|
| Tensile strain | 屈服,23°C | ISO527-2 | 2.9 % |
| Bending stress | ISO178 | 65.0 Mpa | |
| Tensile modulus | ISO527-2 | 2400 Mpa | |
| Tensile stress | 屈服,23°C | ISO527-2 | 43.0 Mpa |
| Flexural modulus | ISO178 | 2000 Mpa |
| Electrical performance | Test Condition | Test Method | BASF KOREA/EGP-7 |
|---|---|---|---|
| Volume resistivity | IEC60093 | 1E+15 ohms·cm |
| flammability | Test Condition | Test Method | BASF KOREA/EGP-7 |
|---|---|---|---|
| UL flame retardant rating | UL94 | HB |
| physical property | Test Condition | Test Method | BASF KOREA/EGP-7 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 0.21 % |
| 饱和,23°C | ISO62 | 0.95 % | |
| Apparent density | 0.55到0.65 g/cm³ | ||
| Melt volume flow rate | 220°C/10.0kg | ISO1133 | 5.00 cm3/10min |
| Shrinkage rate | ISO294-4 | 0.40到0.70 % |
| Thermal performance | Test Condition | Test Method | BASF KOREA/EGP-7 |
|---|---|---|---|
| thermal conductivity | DIN52612 | 0.17 W/m/K | |
| maximum service temperature | 80 °C | ||
| vicat | -- | ISO306/A50 | 107 °C |
| Hot deformation temperature 3 | 1.8MPa,退火 | ISO75-2/A | 101 °C |
| MD | ISO11359-2 | 8.0E-5到1.1E-4 cm/cm/°C | |
| Hot deformation temperature 3 | 0.45MPa,退火 | ISO75-2/B | 103 °C |
| vicat | -- | ISO306/B50 | 100 °C |