Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| density | | ISO 1183 | 1.37 g/cm³ |
| Shrinkage rate | | ISO 294-4 | 0.50to0.70 % |
| Shrinkage rate | | ISO 294-4 | 0.40to0.65 % |
| Water absorption rate | | ISO 62 | 0.030 % |
| flammability | Test Condition | Test Method | Test Result |
|---|
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| UL flame retardant rating | | UL 94 | V-1 |
| UL flame retardant rating | | UL 94 | V-1 |
| Burning wire flammability index | | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | | ASTM D2863 | 30 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Tensile strain | | ISO 527-2/5 | 2.2 % |
| Tensile strain | | ISO 527-2/5 | 2.5 % |
| Tensile modulus | | ISO 527-2/1 | 5000 MPa |
| Tensile modulus | | ISO 527-2/1 | 4300 MPa |
| Tensile modulus | | ISO 527-2/1 | 3600 MPa |
| Tensile modulus | | ISO 527-2/1 | 3200 MPa |
| tensile strength | | ISO 527-2/5 | 20.0 MPa |
| tensile strength | | ISO 527-2/5 | 55.0 MPa |
| tensile strength | | ISO 527-2/5 | 40.0 MPa |
| tensile strength | | ISO 527-2/5 | 20.0 MPa |
| Tensile strain | | ISO 527-2/5 | 1.5 % |
| Tensile strain | | ISO 527-2/5 | 2.0 % |
| Tensile strain | | ISO 527-2/5 | 2.0 % |
| tensile strength | | ISO 527-2/5 | 65.0 MPa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|
| Charpy Notched Impact Strength | | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | | ISO 179/1eU | 15 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| Compared to the Leakage Tracking Index (CTI) | | IEC 60112 | PLC 2 |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat distortion temperature | | ISO 75-2/B | 140 °C |
| Heat distortion temperature | | ISO 75-2/A | 135 °C |
| Continuous use temperature | | | 105 °C |
| vicat | | ISO 306/B50 | 145 °C |
| Linear coefficient of thermal expansion | | ISO 11359-2 | 5E-06 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.