Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPO(PPE)+PS Laril 13-V1KC LATI S.p.A.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LATI S.p.A./Laril 13-V1KC |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 5.0 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 15 kJ/m² |
| Mechanical properties | Test Condition | Test Method | LATI S.p.A./Laril 13-V1KC |
|---|---|---|---|
| tensile strength | 断裂,90°C | ISO 527-2/5 | 40.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/5 | 2.0 % |
| tensile strength | 断裂,120°C | ISO 527-2/5 | 20.0 MPa |
| Tensile strain | Yield,120°C | ISO 527-2/5 | 1.5 % |
| Tensile modulus | 90°C | ISO 527-2/1 | 3600 MPa |
| 23°C | ISO 527-2/1 | 5000 MPa | |
| Tensile strain | 断裂,120°C | ISO 527-2/5 | 2.5 % |
| Tensile modulus | 60°C | ISO 527-2/1 | 4300 MPa |
| tensile strength | 断裂,60°C | ISO 527-2/5 | 55.0 MPa |
| Yield,120°C | ISO 527-2/5 | 20.0 MPa | |
| 断裂,23°C | ISO 527-2/5 | 65.0 MPa | |
| Tensile modulus | 120°C | ISO 527-2/1 | 3200 MPa |
| Tensile strain | 断裂,60°C | ISO 527-2/5 | 2.0 % |
| 断裂,90°C | ISO 527-2/5 | 2.2 % |
| Electrical performance | Test Condition | Test Method | LATI S.p.A./Laril 13-V1KC |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 2 |
| flammability | Test Condition | Test Method | LATI S.p.A./Laril 13-V1KC |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-1 |
| Burning wire flammability index | 1.0mm | IEC 60695-2-12 | 960 °C |
| 2.0mm | IEC 60695-2-12 | 960 °C | |
| UL flame retardant rating | 1.5mm | UL 94 | V-1 |
| Limiting Oxygen Index | ASTM D2863 | 30 % |
| physical property | Test Condition | Test Method | LATI S.p.A./Laril 13-V1KC |
|---|---|---|---|
| Shrinkage rate | MD:2.00mm | ISO 294-4 | 0.40to0.65 % |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.030 % |
| density | ISO 1183 | 1.37 g/cm³ | |
| Shrinkage rate | TD:2.00mm | ISO 294-4 | 0.50to0.70 % |
| Thermal performance | Test Condition | Test Method | LATI S.p.A./Laril 13-V1KC |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 140 °C |
| vicat | ISO 306/B50 | 145 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 135 °C |
| Continuous use temperature | 105 °C | ||
| Linear coefficient of thermal expansion | MD：30到100°C | ISO 11359-2 | 5E-06 cm/cm/°C |