Technical Data Sheet
| hardness | Test Condition | Test Method | Test Result |
|---|
| Rockwell hardness | R-Scale, 23°C | ASTM D785 | 109 |
| thermal performance | Test Condition | Test Method | Test Result |
|---|
| Heat Deflection Temperature | 0.45 MPa, 未Annealed | ASTM D648 | 101 °C |
| Heat Deflection Temperature | 1.8 MPa, 未Annealed | ASTM D648 | 88.0 °C |
| optical performance | Test Condition | Test Method | Test Result |
|---|
| transmissivity | Total | ASTM D1003 | 91.0 % |
| haze | -- | ASTM D1003 | < 1.0 % |
| haze | --3 | Internal Method | < 6.0 % |
| shrinkage rate | Boiling, 1 hr | Internal Method | 1.9 % |
| shrinkage rate | Boiling, 2 hr | Internal Method | 2.3 % |
| shrinkage rate | Dishwasher | Internal Method | 0.0 % |
| Physical properties | Test Condition | Test Method | Test Result |
|---|
| shrinkage rate | Injection，Flow | ASTM D955 | 0.50 - 0.70 % |
| injection | Test Condition | Test Method | Test Result |
|---|
| drying temperature | | | 88 °C |
| drying time | | | 4.0 to 6.0 hr |
| Processing (melt) temperature | | | 260 to 282 °C |
| mold temperature | | | 38 to 66 °C |
| mechanical properties | Test Condition | Test Method | Test Result |
|---|
| tensile modulus | 23°C | ASTM D638 | 1520 Mpa |
| tensile modulus | 23°C | ISO 527-2 | 1540 Mpa |
| tensile strength | Yield, 23°C | ASTM D638 | 45.0 Mpa |
| tensile strength | Yield, 23°C | ISO 527-2 | 44.0 Mpa |
| tensile strength | Break, 23°C | ASTM D638 | 56.0 Mpa |
| tensile strength | Break, 23°C | ISO 527-2 | 55.0 Mpa |
| elongation | Yield, 23°C | ASTM D638 | 6.0 % |
| elongation | Break, 23°C | ASTM D638 | 180 % |
| elongation | Break, 23°C | ISO 527-2 | 150 % |
| bending strength | Yield, 23°C | ASTM D790 | 72.0 Mpa |
| impact performance | Test Condition | Test Method | Test Result |
|---|
| Suspended wall beam without notch impact strength | -40°C | ASTM D4812 | 无断裂 |
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 无断裂 |
| Dart impact | -40°C, Energy at Max Load | ASTM D3763 | 66.0 J |
| Dart impact | 23°C, Energy at Max Load | ASTM D3763 | 57.0 J |
| Dart impact | | Internal Method | No Crazes/No Impact Failures |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.