physical property | Test Condition | Test Method | Test Result |
---|
density | | | 1.12 g/cm³ |
density | | | 1.18 g/cm³ |
Water absorption rate | Equilibrium | ASTM D570 | 0.38 % |
Viscosity | | | 650to750 mPa·s |
hardness | Test Condition | Test Method | Test Result |
---|
Shore hardness | | | 78to80 |
Supplementary Information | Test Condition | Test Method | Test Result |
---|
CriticalExposure | | | 8.30 mJ/cm² |
Puncture Strength | | | 116.8 µm |
Mechanical properties | Test Condition | Test Method | Test Result |
---|
Tensile modulus | | ASTM D638 | 2300to2630 MPa |
tensile strength | | ASTM D638 | 45.0to50.0 MPa |
elongation | Break | ASTM D638 | 7.0to20 % |
Flexural modulus | | ASTM D790 | 2350to2550 MPa |
bending strength | | ASTM D790 | 75.0to79.0 MPa |
Impact resistance | Test Condition | Test Method | Test Result |
---|
Suspended wall beam without notch impact strength | | ASTM D256 | 55to66 J/m |
Thermal performance | Test Condition | Test Method | Test Result |
---|
Heat distortion temperature | | ASTM D648 | 47.0 °C |
Heat distortion temperature | | ASTM D648 | 42.0 °C |
Glass Transition Temperature | | DMA | 52.0 °C |
Linear coefficient of thermal expansion | | ASTME831 | 9.5E-05 cm/cm/°C |
Linear coefficient of thermal expansion | | ASTME831 | 1.8E-04 cm/cm/°C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.