Unspecified White 200 3D Systems
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 3D Systems/ White 200 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D256 | 55to66 J/m |
| hardness | Test Condition | Test Method | 3D Systems/ White 200 |
|---|---|---|---|
| Shore hardness | 邵氏D | 78to80 |
| Supplementary Information | Test Condition | Test Method | 3D Systems/ White 200 |
|---|---|---|---|
| Puncture Strength | 116.8 µm | ||
| CriticalExposure | 8.30 mJ/cm² |
| Mechanical properties | Test Condition | Test Method | 3D Systems/ White 200 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 7.0to20 % |
| tensile strength | ASTM D638 | 45.0to50.0 MPa | |
| Tensile modulus | ASTM D638 | 2300to2630 MPa | |
| Flexural modulus | ASTM D790 | 2350to2550 MPa | |
| bending strength | ASTM D790 | 75.0to79.0 MPa |
| physical property | Test Condition | Test Method | 3D Systems/ White 200 |
|---|---|---|---|
| density | --2 | 1.12 g/cm³ | |
| --3 | 1.18 g/cm³ | ||
| Water absorption rate | 平衡 | ASTM D570 | 0.38 % |
| Viscosity | 30°C | 650to750 mPa·s |
| Thermal performance | Test Condition | Test Method | 3D Systems/ White 200 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 42.0 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 47.0 °C | |
| Linear coefficient of thermal expansion | MD：70到140°C | ASTME831 | 1.8E-04 cm/cm/°C |
| MD：30到50°C | ASTME831 | 9.5E-05 cm/cm/°C | |
| Glass Transition Temperature | DMA | 52.0 °C |