Technical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|
| Specific volume | | | 0.849 cm³/g |
| Shrinkage rate | | ASTM D2566 | 0.14 % |
| Solid content by volume | | | 100 % |
| thermosetting | Test Condition | Test Method | Test Result |
|---|
| Thermosetting components | Hardener | | 按重量计算的混合比:20 |
| Thermosetting components | | | 8.0 min |
| Thermosetting components | Resin | | 按重量计算的混合比:80 |
| Uncured Properties | Test Condition | Test Method | Test Result |
|---|
| Curing Time | | | 3.0 hr |
| hardness | Test Condition | Test Method | Test Result |
|---|
| Shore hardness | Shore A | ASTM D2240 | 88 |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|
| Wear amount | | | 220 mg/1000cycles |
| elastomer | Test Condition | Test Method | Test Result |
|---|
| tensile strength | | ASTM D412 | 16.5 MPa |
| elongation | Break | ASTM D412 | 500 % |
| tear strength | | ASTM D624 | 48.2 kN/m |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|
| dielectric strength | | ASTM D149 | 14 kV/mm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|
| maximum service temperature | | | 82 °C |
| maximum service temperature | | | 49 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.
Compare