PA6 Ultramid® B3M6 GREY Q94 22319
61
- Properties:Flame retardantOil resistantHalogen-free
- Usages:Electrical applicationsIndustrial machinery
CompareTechnical Data Sheet
| physical property | Test Condition | Test Method | Test Result |
|---|---|---|---|
| density | ASTM D792 | 1.36 g/cm³ | |
| ISO 1183 | 1.36 g/cm³ | ||
| Shrinkage rate | 0.90 % | ||
| Water absorption rate | ASTM D570 | 6.2 % | |
| ISO 62 | 6.2 % | ||
| ASTM D570 | 2.4 % | ||
| ISO 62 | 2.4 % |
| Mechanical properties | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 3700 Mpa | |
| tensile strength | ASTM D638 | 85.0 Mpa | |
| ISO 527-2 | 85.0 Mpa | ||
| elongation | ASTM D638 | 4.9 % | |
| Tensile strain | ISO 527-2 | 4.9 % | |
| Flexural modulus | ISO 178 | 3270 Mpa |
| Impact resistance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | 5.6 kJ/m² | |
| Impact strength of cantilever beam gap | ASTM D256 | 45 J/m | |
| ASTM D256 | 64 J/m | ||
| ISO 180 | 4.0 kJ/m² | ||
| ISO 180 | 5.5 kJ/m² |
| Electrical performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Volume resistivity | ASTM D257 | >1.0E+15 ohms·cm | |
| IEC 60093 | >1.0E+15 ohms·cm |
| Thermal performance | Test Condition | Test Method | Test Result |
|---|---|---|---|
| Heat distortion temperature | ASTM D648 | 120 °C | |
| ISO 75-2/A | 70.0 °C | ||
| melting temperature | ASTM D3418 | 220 °C | |
| ISO 3146 | 220 °C | ||
| Heat distortion temperature | ASTM D648 | 195 °C | |
| ISO 75-2/B | 160 °C |
IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.