PA6 B3M6 GREY Q94 22319 BASF SHANGHAI
Ultramid®
Electrical applications、Industrial machinery
Flame retardant、Oil resistant、Halogen-free
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF SHANGHAI/B3M6 GREY Q94 22319 |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTMD256 | 64 J/m |
| -40°C | ISO180 | 4.0 kJ/m² | |
| 23°C | ISO180 | 5.5 kJ/m² | |
| -40°C | ASTMD256 | 45 J/m | |
| Charpy Notched Impact Strength | 23°C | ISO179 | 5.6 kJ/m² |
| Electrical performance | Test Condition | Test Method | BASF SHANGHAI/B3M6 GREY Q94 22319 |
|---|---|---|---|
| VolumeResistivity | 1.50mm | ASTMD257 | >1.0E+15 ohms·cm |
| Volume resistivity | IEC60093 | >1.0E+15 ohms·cm |
| Mechanical properties | Test Condition | Test Method | BASF SHANGHAI/B3M6 GREY Q94 22319 |
|---|---|---|---|
| Tensile modulus | 23°C | ISO527-2 | 3700 Mpa |
| Flexural modulus | 23°C | ISO178 | 3270 Mpa |
| elongation | 断裂,23°C | ASTMD638 | 4.9 % |
| tensile strength | 断裂,23°C | ASTMD638 | 85.0 Mpa |
| Tensile strain | 断裂,23°C | ISO527-2 | 4.9 % |
| Tensile stress | 断裂,23°C | ISO527-2 | 85.0 Mpa |
| physical property | Test Condition | Test Method | BASF SHANGHAI/B3M6 GREY Q94 22319 |
|---|---|---|---|
| Shrinkage rate | MD：3.18mm | 0.90 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO62 | 2.4 % |
| 饱和,23°C | ISO62 | 6.2 % | |
| density | ASTMD792 | 1.36 g/cm³ | |
| ISO1183 | 1.36 g/cm³ | ||
| Water absorption rate | 饱和 | ASTMD570 | 6.2 % |
| 平衡,50%RH | ASTMD570 | 2.4 % |
| Thermal performance | Test Condition | Test Method | BASF SHANGHAI/B3M6 GREY Q94 22319 |
|---|---|---|---|
| ASTMD3418 | 220 °C | ||
| 0.45MPa,未退火 | ASTMD648 | 195 °C | |
| 0.45MPa,未退火 | ISO75-2/B | 160 °C | |
| 1.8MPa,未退火 | ISO75-2/A | 70.0 °C | |
| ISO3146 | 220 °C | ||
| 1.8MPa,未退火 | ASTMD648 | 120 °C |