ABS PULSE™ 920 MG

Usages:
Applications in the automotive field
automotive internal components
Compare

Technical Data Sheet

physical property	Test Condition	Test Method	Test Result
Shrinkage rate		ISO294-4	0.35to0.45 %
Water absorption rate	Saturation	ISO622	0.030 %
Water absorption rate	Water absorption rate	Equilibrium	ISO622	0.28 %
VOCContent		VDA277	9.00 µg/g
density		ISO1183/B	1.12 g/cm³
density	density		ISO11832	1130 kg/m³
Apparent density		ISO60	0.65 g/cm³
melt mass-flow rate		ISO1133	17 g/10min
Melt volume flow rate		ISO11332	15.0 cm³/10min
SpiralFlow			51.0 cm

flammability	Test Condition	Test Method	Test Result
Burning Behav.		ISO12102	HB

Impact resistance	Test Condition	Test Method	Test Result
Charpy impact strength		ISO179/1eU2	NoBreak
CharpyImpactStrength		ISO179/1eU2	NoBreak
Charpy Notched Impact Strength		ISO179/1eA	7.0 kJ/m²
Charpy Notched Impact Strength	Charpy Notched Impact Strength		ISO179/1eA	22 kJ/m²
CharpyNotchedImpactStrength		ISO179/1eA2	45.0 kJ/m²
Charpy Notched Impact Strength		ISO179/1eA2	30.0 kJ/m²

Mechanical properties	Test Condition	Test Method	Test Result
Tensile modulus		ISO527-2/1	2250 MPa
Tensile modulus	Tensile modulus		ISO527-22	2050 MPa
Tensile stress	Yield	ISO527-22	48.0 MPa
Tensile strain	Yield	ISO527-22	4.6 %
Tensile strain	Tensile strain	Break	ISO527-2/50	100 %
Nominal strainatbreak		ISO527-22	>50 %
Flexural modulus		ISO178	2100 MPa
Tensile stress	Yield	ISO527-2/50	50.0 MPa

Thermal performance	Test Condition	Test Method	Test Result
		ISO75-22	126 °C
			ISO75-2/A	105 °C
				ISO75-22	102 °C
vicat		ISO306/B50	122 °C
vicat	vicat		ISO3062	128 °C
		ISO11359-2	7.3E-05 cm/cm/°C

IMPORTANT NOTES: Plas.com collected the data in the data sheet from the material manufacturers. Plas.com makes the best effort to improve the accuracy of the data, but has no responsibility for the data. We strongly recommend verifying the validity of the data with the material manufacturers before making a final decision.

Get App