ABS PULSE™ 920 MG Trinseo
--
Applications in the automotive field, automotive internal components
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Trinseo/PULSE™ 920 MG |
|---|---|---|---|
| Charpy Notched Impact Strength | -30°C | ISO 179/1eU2 | NoBreak |
| 23°C | ISO 179/1eU2 | NoBreak | |
| 23°C | ISO 179/1eA | 22 kJ/m² | |
| -30°C | ISO 179/1eA | 7.0 kJ/m² | |
| -30°C | ISO 179/1eA2 | 30.0 kJ/m² | |
| 23°C | ISO 179/1eA2 | 45.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Trinseo/PULSE™ 920 MG |
|---|---|---|---|
| Tensile modulus | ISO 527-22 | 2050 MPa | |
| Tensile strain | 屈服 | ISO 527-22 | 4.6 % |
| Nominal fracture strain | ISO 527-22 | >50 % | |
| tensile strength | 屈服 | ISO 527-22 | 48.0 MPa |
| Flexural modulus | ISO 178 | 2100 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
| Tensile modulus | ISO 527-2/1 | 2250 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 50.0 MPa |
| flammability | Test Condition | Test Method | Trinseo/PULSE™ 920 MG |
|---|---|---|---|
| Burning Behav. | 1.60mm,UL | ISO 12102 | HB |
| physical property | Test Condition | Test Method | Trinseo/PULSE™ 920 MG |
|---|---|---|---|
| Water absorption rate | 饱和 | ISO 622 | 0.030 % |
| Shrinkage rate | ISO 294-4 | 0.35to0.45 % | |
| density | ISO 1183/B | 1.12 g/cm³ | |
| Apparent density | ISO 60 | 0.65 g/cm³ | |
| VOCContent | VDA277 | 9.00 µg/g | |
| melt mass-flow rate | 260°C/5.0kg | ISO 1133 | 17 g/10min |
| Melt volume flow rate | 260°C/5.0kg | ISO 11332 | 15.0 cm³/10min |
| spiral flow length | 51.0 cm | ||
| density | ISO 11832 | 1130 kg/m³ | |
| Water absorption rate | 平衡 | ISO 622 | 0.28 % |
| Thermal performance | Test Condition | Test Method | Trinseo/PULSE™ 920 MG |
|---|---|---|---|
| vicat | 50N | ISO 3062 | 128 °C |
| ISO 306/B50 | 122 °C | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 105 °C |
| 1.8MPa，HDT | ISO 75-22 | 102 °C | |
| Linear coefficient of thermal expansion | MD：-30到80°C | ISO 11359-2 | 7.3E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa，HDT | ISO 75-22 | 126 °C |